Abstract
The deformation characteristics of quenched and aged Ti-V alloys in the composition range 20 to 40 wt pct vanadium have been examined by optical metallography and transmission electron microscopy. A coarse lenticular deformation product similar in appearance to previously reported strain induced “martensites” was found to be associated with the occurrence of the omega phase. These features proved to be {112}〈111〉 twins. In the omega bearing alloys prolonged aging resulted in a transition of the deformation mode from twinning to slip at a point which corresponded either to the onset of embrittlement or alpha phase precipitation.
Similar content being viewed by others
References
Fu-Wen Ling, H. J. Rack, E. A. Sarke, and Jr.:Met. Trans., 1973, vol. 4, p. 1671.
Fu-Wen Ling, E. A. Sarke, Jr., and B. G. LeFevre:Met. Trans., 1974, vol. 5, p. 179.
J. C. Williams and M. J. Blackburn:Trans. TMS-AIME, 1969, vol. 245, p. 2352.
C. G. Rhodes:Metallogr., 1969, vol. 2, p. 257.
M. J. Blackburn and J. C. Williams:Trans. TMS-AIME, 1968, vol. 242, p. 2461.
B. S. Hickman:J. Inst. Metals, 1968, vol. 96, p. 2487.
J. C. Williams, B. S. Hickman, and H. L. Marcus:Met. Trans., 1971, vol. 2, p. 1913.
M. K. Koul and J. F. Breedis:Met. Trans., 1970, vol. 1, p. 1451.
E. Levine, S. Hayden, and H. Margolin:Acta Met., 1974, vol. 22, p. 1443.
D. N. Williams, R. A. Wood, and E. S. Bartlett:Met. Trans., 1972, vol. 3, p. 1529.
J. A. Robertson, S. Fujishiro, V. S. Arunachalam, and C. M. Sargent:Met. Trans., 1974, vol. 5, p. 2317.
H. J. Rack, D. Kalish, and K. D. Fike:Mater. Sci Eng., 1970, vol. 6, p. 181.
M. J. Blackburn and J. A. Feeney:J. Inst. Metals, 1971, vol. 99, p. 132.
J. C. Williams:Proc. Sec. Int. Conf. on Ti, MIT, Ti Sci and Tech., p. 1433, Jaffee and Burte, eds., Plenum Press, N. Y., 1973.
J. M. Silcock:Acta Met., 1953, vol. 6, p. 481.
J. C. Williams, D. de Fontaine, and N. E. Paton:Met. Trans., 1973, vol. 4, p. 2701.
D. de Fontaine, N. E. Paton, and J. C. Williams:Acta. Met., 1971, vol. 19, p. 1153.
B. S. Hickman:J. Mater. Sci., 1969, vol. 4, p. 554.
T. S. Kuan, R. R. Ahrens, and S. L. Sass:The Stress Induced Omega Transformation in Ti-V Alloys, Report 2335, The Materials Research Center, Cornell University, Ithaca, New York, 1975.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Paris, H.G., LeFevre, B.G. & Starke, E.A. Deformation behavior in quenched and aged beta Ti-V alloys. Metall Trans A 7, 273–278 (1976). https://doi.org/10.1007/BF02644467
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02644467