Abstract
Directional solidification of Pb-Sn eutectic alloys at high temperature gradients has shown that two distinct eutectic morphologies occur, a regular lamellar structure and a wavy lamellar structure, termed degenerate. An electron channelling technique was used to characterize the crystallography of the two morphologies. The degenerate grains grow in advance of the regular grains and are the preferred growth morphologies in spite of the fact that coarsening experiments revealed that the degenerate grains possessed a higher lamellar interface energy. This result conflicts with the Zener model of eutectic growth. A possible rationalization of this conflict based on the anisotropy of thermal conductivity in Sn is presented.
Similar content being viewed by others
References
R. H. Hopkins and R. W. Kraft:Trans. TMS-AIME, 1968, vol. 242, p. 1627.
R. W. Kraft:Trans. TMS-AIME, 1961, vol. 221, p. 704.
N. Takahashi and K. Schinuma:J. Inst. Metals, 1958-59, vol. 87, p. 19.
B. La Bulle and C. Petipas:J. Cryst. Growth, 1975, vol. 28, p. 279.
K. N. Tu and D. Turnbull:Acta Met, 1969, vol. 17, p. 1263.
L. M. Hogan, R. W. Kraft, and F. D. Lemkey:Advances in Materials Research, vol. 5, p. 81, H. Herman, ed., Wiley, New York, N.Y., 1971.
W. Kutz and P. R. Sahm:Gerichtet Erstarrte Eutektische Werkstoffe, p. 319, Springer-Verlag, New York, N.Y., 1975.
J. D. Verhoeven and E. D. Gibson:J. Cry. Growth, 1971, vol. 11, p. 29.
J. D. Verhoeven and E. D. Gibson:Met. Trans., 1971, vol. 2, p. 3021.
E. D. Gibson and J. D. Verhoeven:J. Phys. E., in press.
J. D. Verhoeven and E. D. Gibson:Chanelling Patterns from 1ώm Particles Using the Stereoscan S-4, Report: IS-3169, 1975.
C. G. van Essen and J. D. Verhoeven:J. Phys. E., 1974, vol. 7, p. 768.
J. D. Verhoeven and E. D. Gibson:Met. Trans., 1972, vol. 3, p. 1893.
J. D. Verhoeven and E. D. Gibson:Met. Trans., 1973, vol. 4, p. 2581.
D. P. Mourer and J. D. Verhoeven:J. Cryst. Growth, 1977, vol. 37 p. 197.
J. D. Livingston and J. W. Cahn:ActaMet., 1974, vol. 22, p. 495.
W. A. Tiller:Liquid Metals and Solidification, p. 276, ASM, Cleveland, Ohio, 1958.
J. D. Hunt: Ph.D. Thesis, Cambridge University, Cambridge, England, 1963.
F. Weinberg and B. Chalmers:Can. J. Phys., 1951, vol. 23, p. 382.
S. O’Hare:ActaMet., 1967, vol. 15, p. 231.
C. Zener:Trans. AIME, 1946, vol. 167, p. 550.
M. Hülert:Jemkontorets Ann., 1957, vol. 141, p. 757.
K. A. Jackson and J. D. Hunt:Trans. TMS-AIME, 1966, vol. 236, p. 1129.
R. K. Trivedi: Private communication, Iowa State University, 1976.
M. N. Croker, R. S. Fidler, and R. W. Smith:J. Cryst. Growth, 1971, vol. 11, p. 121.
A. Moore and R. Elliott:Solidification of Metals, p. 176, I.S.I. Publ. 110, Iron Steel Inst., London, 1968.
R. M. Jordan and J. D. Hunt:Met. Trans., 1972, vol. 3, p. 1385.
Author information
Authors and Affiliations
Additional information
An erratum to this article is available at http://dx.doi.org/10.1007/BF02646896.
Rights and permissions
About this article
Cite this article
Verhoeven, J.D., Gibson, E.D. & Mourer, D.P. The morphology and crystallography of directionally solidified pb-sn eutectic alloys. Metall Trans A 8, 1239–1247 (1977). https://doi.org/10.1007/BF02643838
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02643838