Abstract
Precipitation hardening at room temperature (natural aging) and isothermal precipitation hardening at 422 to 455 K beyond the point of peak strength (overaging) were studied. Natural aging kinetics of the increase in strength and resistivity were comparable with those of alloy 7075. Alloy 7050, however, develops peak strength by aging at higher temperatures. This ability of 7050 to develop peak strength upon aging in the temperature region used to improve the resistance to stress-corrosion cracking and toughness of 7XXX alloys is attributed to the effect of Cu on increasing the temperature range of G.P zone stability.
Similar content being viewed by others
References
J. T. Staley, H. Y. Hunsicker, and R. Schmidt: “New Aluminum Alloy 7050,” TMS paper selection, 1971.
H. Y. Hunsicker:Aluminum, Vol. 1, K. R. Van Horn, ed., p. 124, ASM, Metals Park, 1967.
B. W. Lifka and D. O. Sprowls:Localized Corrosion-Cause of Metal Failure, p. 135, ASTM STP 516, American Society for Testing and Materials, 1972.
J. T. Staley: unpublished work, 1968.
J. Smugeresky, H. Herman, and S. R. Pollack:Acta Met., 1969, vol. 17, p. 883.
J. T. Staley: “Investigation to Improve the Stress-Corrosion Resistance of Aluminum Aircraft Alloys Through Alloy Additions and Specialized Heat Treatment,” Final Report on Naval Air Systems Contract N00019-68-C-0146, February 1969, Appendix Table 2.
G. W. Lorimer and R. B. Nicholson:The Mechanism of Phase Transformations in Crystalline Solids, p. 36, London, Inst. of Met., Monograph 33, 1969.
M. H. Jacobs and D. W. Pashley:The Mechanism of Phase Transformations in Crystalline Solids, p. 43, London, Inst. of Met., Monograph 33, 1969.
1. J. Polmear and P. S. Young:J. Inst. Metals, 1958-59, vol. 87, p. 65.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Staley, J.T. Aging kinetics of aluminum alloy 7050. Metall Trans 5, 929–932 (1974). https://doi.org/10.1007/BF02643150
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02643150