Investigation of eutectic transformation of Zn−Al alloy by DTA

Abstract

The paper discusses the investigation of crystallization of metals and alloys by differential thermal analysis (DTA). It was assumed that this method allows determination of the mechanism and kinetics of volumetric crystallization underiso conditions (e.g. anisothermal) on the basis of the parameters of the equation expressing an integral form of the DTA curve. From DTA, a course of eutectic transformation was determined for a technical Zn−Al alloy containing 4wt% Al. Investigations were carried out under continuous cooling at various rates and the kinetics parameters were determined with the KEKAM equation:-ln(1-x)=kl _n

Zusammenfassung

Man hat eine Auffassung der Untersuchung des Kristallisationsverfahrens von Metallen, Metallegierungen und Legierungen mittells der thermischen Differenzanalyse—DTA dargestellt.

Es wurde angenommen, daß dieses Verfahren den Mechanismus und die Kinetik der Volumenkristallisation unter iso-als auch anisothermishcen Bedingungen in Anlehnung an die Parameter der Gleichung bestimmen läßt, welche die vollständige Form der DTA—Kurve beschreibt. Auf Grundlage der Untersuchungen von DTA wurde der Ablauf von eutektischer Umwandlung in der technischen Legierung Zn−Al mit Gehalt von 4% Al bestimmt. Die Untersuchungen wurden in Bedingungen der ununterbrochenen Abkühlung mit unterschiedliches Geschwindigkeiten durchgeführt. Man hat kinetischen Parameter vom Verfahren der eutektischen Kristallisation in Anlehnung an die KEKAM-Gleichung-ln(1-x)=kl ⁿ bestimmt.