Calorimetric study of blends of poly(butylene terephthalate) and liquid crystalline copolyester

Abstract

A calorimetric study of blends of poly(ethylene terephthalate-co-p-oxybenzoate), PET/PHB, with poly(butylene terephthalate), PBT has been carried out in the form of as-spun and drawn fibres. DSC melting and crystallization results show that PBT is compatible with LCP and the crystallization of PBT decreases by the addition of LCP in the matrix. The crystallization behaviour of blend fibres is investigated as a function of temperature of crystallization. A detailed analysis of the crystallization course has been made utilizing the Avrami expression. The isothermal calorimetric measurements provide evidence of decrease of rate of crystallization of PBT on addition of the liquid crystalline component up to about 50% by weight. The values of the Avrami exponents change in the temperature range from 200° to 215°C. Dimensionality changes in crystallization could be due to LCP mesophase-transition.

Zusammenfassung

Es wurde eine kalorimetrische Untersuchung von Gemischen von Poly(ethylen-terephthalat-co-p-oxybenzoat), PET/PHB mit Poly(Butylen-terephtalat), PTB durchgefürt. Die DSC Schmelz- und Kristallisationsergebnisse zeigen, daß PBT kompatibel mit LCP ist und daß die Kristallisation von PBT durch Zusatz von LCP in der Matrix abnimmt. Das Kristallisationsverhalten der Gemischfibern wurde in Abhängigkeit von der Kristallisations-temperatur untersucht. Unter Anwendung der Avrami-Gleichung wurde eine ausführliche Analyse des Kristallisationsweges erstellt. Die isothermen kalorimetrischen Messungen bestätigen die Abnahme der Kristallisationsgeschwindigkeit von PBT bei Zusatz der Flüssigkristallkomponente bis zu 50 Gew %. Im Temperaturbereich variieren die Avrami Exponenten zwischen 200° und 215°C. Dimensionsänderungen der Kristallisation könnten der LCP Mesophasenumwandlung zugeschrieben werden.