Abstract
The plasma nitriding behaviour of Fe-18Cr-9Ni alloy was compared with gas nitriding. The alloy was nitrided under the following conditions: specimen temperature: 823 K, nitriding time: mainly 108 ks, total pressure: 0.4–0.7 kPa, mixture ratio of N2 and H2∶ 0.25, discharge voltage: 350–450 V, current: 0.8–1.1 A. Formation of a surface layer of iron nitrides was not observed. Formation of a homogeneous internal nitriding layer, consisting of small precipitates of CrN and the γ-phase matrix, was, however, noted. The lattice constant at the specimen surface was smaller than that at greater depth. This may have been because the sputtering effect decreased the dissolved nitrogen content at the specimen surface. The sputtering of iron nitrides at the specimen surface by the plasma was experimentally confirmed through γ′-Fe4N formation on Si beside an alloy specimen. The characteristics of the plasma nitriding mentioned above are discussed in relation to the sputtering.
Similar content being viewed by others
References
H. Kuwahara, H. Matsuoka, J. Takada andI. Tamura,J. Jpn. Plating Coating,10 (1990) 54.
Metals Handbook, Heat treating, edited by American Society for Metals 9th Edn, Vol. 4 (Metals Park, Ohio, 1981).
B. Billon andA. Hendry,Surf. Eng. 1 (1985) 114.
H. Kuwahara, J. Takada andI. Tamura in Proceedings of the 7th International Symposium on Plasma Chemistry, Eindhoven, July 1985, edited byC. J. Timmermans (International Union of Pure and Applied Chemistry, Eindhoven, 1985). 473.
H. Kuwahara, H. Matsuoka, Y. Tomii, S. Kikuchi, J. Takada andT. Takayama,J. Mater. Sci.,25 (1990) 4120.
L. E. Kindlimann andG. S. Ansell,Metall. Trans. 1 (1970) 163.
J. M. Silcock,Metal Sci. 14 (1978) 561.
B. Mortmer, P. Grieveson andK. H. Jack,Scand. J. Metall. 1 (1972) 203.
B. N. Chapman in “Glow Discharge Processes: Sputtering and Plasma Etching” (John Wiley & Sons, Inc., New York, 1980)
M. Hudis,J. Appl. Phys. 44 (1973) 1489.
Metals Data Book, edited by Japanese Society of Metals (Maruzen, Tokyo, 1974)
M. Tsuchiya, M. Izumiyama andY. Imai,J. Jpn. Inst. Metal. 29 (1965) 427.
G. Faninger andA. Freibmuth,Acta. Phys. Austrica,18 (1964) 280.
M. Kikuchi, T. Tanaka, K. Hamagami, Y. Ogura andR. Tanaka,Metall. Trans. 7A (1976) 906.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kuwahara, H., Matsuoka, H., Tamura, I. et al. Effect of plasma on nitriding of Fe-18Cr-9Ni alloy. J Mater Sci 27, 637–640 (1992). https://doi.org/10.1007/BF02403871
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02403871