The strength of spider silk

  • Papers
  • Published:
Journal of Materials Science Aims and scope Submit manuscript


Tensile tests have been made on the draglines of the Queensland Bird-Catching Spider (Nephila maculata): the masses of the several spiders varied by a factor of about 25. The nominal fracture strength of the silk was independent of the spider size and was about 1100 MPa (the true fracture strength was about 1500 MPa). Larger spiders extruded proportionately thicker draglines and the maximum force which a dragline could sustain was generally two or three times the body weight of the spider. Draglines consisted of two or four individual threads and some tests were made of the properties of these constituent strands. Tests made on draglines aged for 21 days showed only a moderate deterioration in properties although a marked change occurred in the initial part of the stress-strain curve.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others


  1. J. R. Benton,Amer. J. Sci.24 (1907) 75.

    Article  Google Scholar 

  2. F. Lucas,Discovery25 (1964) 20.

    Google Scholar 

  3. M. Denny,J. Exp. Biol.65 (1976) 483.

    Google Scholar 

  4. R. W. Work,Textile Res. J.46 (1976) 485.

    CAS  Google Scholar 

  5. K. C. McKeown, “Spider Wonders of Australia” (Angus and Robertson, Sydney, 1936) pp. 220.

    Google Scholar 

  6. S. L. Kwolek (to du Pont), US Patent 3 671 542 (1972).

  7. T. A. Hancock, J. E. Spruiell andJ. L. White,J. Appl. Polymer Sci.12 (1977) 1227.

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations


Rights and permissions

Reprints and permissions

About this article

Cite this article

Griffiths, J.R., Salanitri, V.R. The strength of spider silk. J Mater Sci 15, 491–496 (1980).

Download citation

  • Received:

  • Accepted:

  • Issue Date:

  • DOI: