EPR in non-doped irradiated polyacetylene

  • O. Holá
  • A. Staško
  • M. Földesová


The influence of γ-irradiation on the paramagnetic properties of non-doped polyacetylene at low and high radiation doses has been studied and summarized. The dependence of the EPR spectra on the radiation dose in irradiated polyacetylene has been measured. No essential changes of the spin mobility as a consequence of irradiation were observed. Our measurements of spin concentration confirm the high resistivity of non-doped polyacetylene to radiation.


Radiation Physical Chemistry Inorganic Chemistry Radiation Dose High Resistivity 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    P. Nagels, H. Krikor,Synt. Met., 28 (1989) D 253.CrossRefGoogle Scholar
  2. 2.
    K. Yoshino, S. Hayashi, K. Kaneto, J. Okube, T. Moriya, T. Matsuyama, H. Yamaoka,Mol. Cryst. Liq. Cryst., 121 (1985) 255.Google Scholar
  3. 3.
    H. Shirakawa, T. Ito, S. Ikeda,Polym. J., 4 (1973) 460.Google Scholar
  4. 4.
    O. Holá, A. Staško, M. Földesová,Acta Phys. Slov., 39 (1989) 371.Google Scholar
  5. 5.
    O.Holá, M. Földesová,J. Radioanal. Nucl. Chem., Lett., 146 (1990) 103.Google Scholar
  6. 6.
    O. Holá, A. Staško, M. Földesová,J. Radioanal. Nucl. Chem., Lett., 165 (1992) 71.Google Scholar
  7. 7.
    B.R. Weinberger, E. Ehrenfreund, A. Pron, A.J. Heeger, A.G. Mac Diarmid,J. Chem. Phys., 72 (1980) 4749.CrossRefGoogle Scholar
  8. 8.
    H. Yamaoka, T. Matsuyama et al.,Rad. Phys. Chem., 37 (1991) 111.Google Scholar
  9. 9.
    K. Tanaka, T. Koike, et al.,Solid State Comun., 49 (1984) 165.CrossRefGoogle Scholar

Copyright information

© Akadémiai Kiadó 1993

Authors and Affiliations

  • O. Holá
    • 1
  • A. Staško
    • 1
  • M. Földesová
    • 1
  1. 1.Faculty of Chemical TechnologySlovak Technical UniversityBratislavaSlovak Republic

Personalised recommendations