Physico-chemical transformations during heating of phosphorites

  • T. Kalyuvee
  • M. Veiderma
  • K. Tynsuaadu
  • H. Vilbok
Inorganic Chemistry, Glass, Ceramics

Abstract

The thermal behaviour of phosphorites in an oxygen or helium atmosphere was studied by means of simultaneous TG-DTG-DTA-gas titrimetric EGA. Thermal oxidation and/or decomposition steps of the contaminating organic materials, carbonate minerals and pyrite, and of the fluorocarbonate-apatite were identified. The evolution of CO2 from the latter has its maximum at 750–850 °C and is accompanied by an increase in the lattice parametera0.

Keywords

Oxidation Oxygen Polymer Atmosphere Physical Chemistry 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Zusammenfassung

Das thermische Verhalten von Phosphoriten in Sauerstoff- oder Heliumatmosphäre wurde durch simultane TG-DTG-DTA-EGA (mittels Gastitrimetrie) untersucht. Thermische Oxidations- und/oder Zersetzungsschritte der Verunreinigungen (organische Materialien, Carbonatminerale und Pyrit) und des Calcium-fluoro-carbonat-apatit wurden identifziert. Die CO2-Abspaltung aus dem letzteren hat ihr Maximum bei 750–850 °C, sie ist begleitet von einer Vergrösserung des Gitterparametersa0.

Резюме

Совмещенным методом ТГ, ДТГ, ДТА и га-титриметрическог о АВГ изучено термическое поведен ие фосфоритов в атмос фере кислорода и гелия. Иде птифицированы отдельные стадии тер мического окисления и (или разложения примесны х органических вещес тв, карбонатных минерал ов, пирита и фторокарбонатапати та. Выделение двуокис и углерода из последнего материал а было максимальным п ри температуре 750–850° и соп ровождалось увеличением парамет ра решетки а0.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. Paulik, F. Paulik and M. Arnold, J. Thermal Anal., 25 (1982) 327.CrossRefGoogle Scholar
  2. 2.
    J. Paulik, F. Paulik and M. Arnold, J. Thermal Anal., 29 (1984) 333.Google Scholar
  3. 3.
    S. R. Silvermann, R. K. Puyat and I. D. Keiser, Amer. Mineralogist, 37 (3–4) (1952) 211.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1988

Authors and Affiliations

  • T. Kalyuvee
    • 1
  • M. Veiderma
    • 1
  • K. Tynsuaadu
    • 1
  • H. Vilbok
    • 1
  1. 1.Department of ChemistryTallinn Technical UniversityUSSR

Personalised recommendations