Kinetics of the formation of whewellite and weddelite by displacement reactions

  • G. Wiedemann
  • G. Bayer
Inorganic Chemistry, Glass, Ceramics

Abstract

The nucleation and crystallization of whewellite and weddelite during displacement reactions has been investigated by means of thermomicroscopy, thermogravimetry, X-ray diffraction, and scanning electron microscopy. Gypsum cleavage plates were immersed at different temperatures in solutions of oxalic acid and alkali oxalates. The reaction product (whewellite and/or weddelite) formed on the gypsum crystal surface. Depending on the concentration of the solution and on the time and temperature, different degrees of reaction, which means varying amounts and crystal forms or Ca-oxalate were found. An evaluation of the growth rate was possible by means of thermogravimetry. Conditions for the preparation of pure weddelite by precipitation from solutions have been established.

Keywords

Polymer Precipitation Growth Rate Electron Microscopy Scanning Electron Microscopy 

Zusammenfassung

Keimbildung und Kristallisation von Whewellit und Weddelit bei Verdrängungsreaktionen wurden durch Thermomikroskopie, Thermogravimetrie, Röntgenbeugung und Rasterelektronenmikroskopie untersucht. Gipsspaltplättchen wurden bei verschiedenen Temperaturen in Oxalsäure- und Natriumoxalatlösungen eingetaucht. Das Reaktionsprodukt (Whewellit oder Weddelit) bildete sich auf der Oberfläche des Gipskristalls. In Abhängigkeit von der Konzentration der Lösung, der Zeit und der Temperatur wurden verschiedene Umsetzungen, d. h. verschiedene Menge und Kristallformen von Calciumoxalat gefunden. Die Wachstumsgeschwindigkeit ließ sich aus thermogravimetrischen Messungen ermitteln. Die Bedingungen zur Herstellung reinen Weddelits durch Fällung aus der Lösung wurden ermittelt.

Резюме

Методами термограви метрии, термомикроск опии, рентгенофазового ан ализа и сканирующей электро нной микроскопии изу чено образование центров кристаллизации и кристаллизация веве ллита и ведделита в пр оцессе реакций смещения. Рас щепленные пластинки гипса были погружены при различных темпер атурах в растворы щавелевой к ислоты и ее щелочных солей. Проду кты реакции (вевеллит или ведделит) образовыва лись на кристаллической пов ерхности гипса. В зави симости от концентрации раство ра, времени погружения и темпера туры раствора, устано влены различные степени ре акции, означающие различные количеств а и кристаллические ф ормы образующегося оксал ата кальция. Термогравиметричес ки проведена оценка с корости реакции роста криста ллов. Определены условия получения чи стого ведделита путе м осаждения из растворов.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    A. Frey-Wissling, Amer. J. Bot., 68 (1) (1981) 130–141.Google Scholar
  2. 2.
    H. J. Arnott, F. G. E. Pautard and H. Steinfink, Nature, 28 (1965) 1197–1198.Google Scholar
  3. 3.
    G. Cocci, Atti Acad. Naz. Lincei Cl. Sci. Fis. Mat. Nat., 31 (1961/62) 292–298.Google Scholar
  4. 4.
    C. Sterling, Acta Cryst., 18 (1965) 917–921.CrossRefGoogle Scholar
  5. 5.
    G. Schubert, G. Brien und C. Bick, VI. Jenaer Harnsteinsymposium 1980, 14–24. Verö ffentlichung der Friedr. Schiller Universität, Jena, 1980.Google Scholar
  6. 6.
    R. T. Marano, J. L. McAtee et al. Thermochim. Acta 4 (1972) 405–409.CrossRefGoogle Scholar
  7. 7.
    G. A. Rose and C. Woodfine, Brit. Jour. of Urology, 48 (1976) 403–412.Google Scholar
  8. 8.
    Mettler Thermal Techniques Series, Technical Bulletin T-104 (1968).Google Scholar
  9. 9.
    D. Dollimore, T. E. Jones and P. Spooner, J. Chem. Soc., A (1970) 2809.Google Scholar
  10. 10.
    Y. Masuda, Y. Ito, R. Ito and K. Iwata, Thermochim. Acta, 99 (1986) 205–215.CrossRefGoogle Scholar
  11. 11.
    H.-J. Schneider, W. Götz und K. Heide, Der Harnstein, S. 87–181 (1973), VEB Gustav Fischer-Verlag, Jena, 1973.Google Scholar
  12. 12.
    G. Bayer and H. G. Wiedemann, Thermochim. Acta, 114 (1987) 75–82.CrossRefGoogle Scholar
  13. 13.
    W. Vahlensieck, Urolithiasis 1, Springer-Verlag Berlin, Heidelberg New York, 1979.Google Scholar
  14. 14.
    H. G. Wiedemann und A. van Tets, Die Naturwissenschaften, 54 (1967) 442.CrossRefGoogle Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1988

Authors and Affiliations

  • G. Wiedemann
    • 1
  • G. Bayer
    • 2
  1. 1.Mettler Instrumente AGGreiffenseeSchweiz
  2. 2.Institut für KristallographieETH ZürichZürichSchweiz

Personalised recommendations