Abstract

Experiments on the coking rates of variously prepared nickel catalysts on TiO2, Al2O3 and MgO in n-butane steam reforming show that changes in the relative coking rate at a rising steam excess in the gas phase depend mainly on the kind of support. The results obtained are accounted for by changes in the electron density at the site of nickel crystallite contact with the surface of various supports.

Keywords

TiO2 Physical Chemistry Nickel Al2O3 Steam 

Abstract

Исследование скорости коксования никелевых катализаторов, приготовленных различным образом на TiO2, Al2O3 и MgO, в паровом крекинге н-бутана указывают на то, что изменения в относительной скорости коксования, при возрастающем избытке водяного пара в газовой фазе, зависят, в основном, от типа носителя. Полученные результаты приписывают изменениям электронной плотности на месте контакта никелевого кристаллита с поверхностью различных носителей.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. R. Rostrup-Nielsen, P. B. Tottrup: Symp. Science of Catal. Appl. in Industry, FPDIE Sindri, No. 39, 379, 1979.Google Scholar
  2. 2.
    Catalyst Handbook, Wolfe Scientific Books, London 1970.Google Scholar
  3. 3.
    J. R. Rostrup-Nielsen: Steam Reforming Catalysts., Teknisk Forlag A/S, Copenhagen 1975.Google Scholar
  4. 4.
    S. P. S. Andrew: Ind. Eng. Chem. Prod. Res. Dev.,8, 321 (1969).CrossRefGoogle Scholar
  5. 5.
    J. Barcicki, T. Borowiecki, A. Machocki, B. Chmiel: Chem. Stos.25, 495 (1981).Google Scholar
  6. 6.
    T. Borowiecki: Appl. Catal.,4, 223 (1982).CrossRefGoogle Scholar
  7. 7.
    T. Borowiecki: Appl. Catal.,10, 273 (1984).CrossRefGoogle Scholar
  8. 8.
    G. J. Epifanov: Solid State Physics, Moskow 1979.Google Scholar
  9. 9.
    A. Machocki: Polish J. Chem.,56, 781 (1982).Google Scholar
  10. 10.
    V. S. Fomenko, I. Podcherniaeva: Emissionnye i adsorbtsionnye svcistva veshchestv i materialov. Moskva 1975.Google Scholar
  11. 11.
    F. F. Volkenstein: Fiziko-khimia povierkhnosti poluprovodnikov. Izd. Nauka, Moskva 1973.Google Scholar

Copyright information

© Akadémiai Kiadó 1987

Authors and Affiliations

  • T. Borowiecki
    • 1
  1. 1.Department of Chemical TechnologyInstitute of Chemistry Maria Curie-Sklodowska UniversityLublinPoland

Personalised recommendations