The oxidic phase FeMoVO7 of the Fe2O3-V2O5-MoO3 system has been synthesized. Susceptibility measurements from 4.2 K to room temperature display an antiferromagnetic behaviour with an effective magnetic moment of 5.80ώ b . This value, and the measured Mössbauer isomer shift of 0.40±0.02 mm/s, are characteristic of high-spin Fe(III). The lowT n value of 15 K suggests a weak interaction among the Fe-O polyhedra. The relative small QS=0.28±0.02 mm/s found in this compound shows that the Fe-O polyhedra symmetry is close to octahedral and almost undistorted.
Similar content being viewed by others
References
M. Kurzawa, Thermochim. Acta 189 (1991) 129.
M. Walczac, M. Kurzawa and E. Filipek, J. Thermal Analysis 31 (1986) 271.
L.J. de Jongh and A.R. Miedema, Adv. Phys. 23 (1974) 1.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Goya, G.F., Mercader, R.C., Vassallo, M.B. et al. Mössbauer and susceptibility studies of FeMoVO7 . Hyperfine Interact 83, 199–201 (1994). https://doi.org/10.1007/BF02074272
Issue Date:
DOI: https://doi.org/10.1007/BF02074272