Abstract
Superconducting YBa2Cu2.955Fe0.045O7 has been studied at temperatures between 300 and 1000 K. Spectra were recorded on a sample which was sealed as a pellet pressed with boron nitride. An atmosphere of oxygen was maintained in the sample region at all times. At temperatures up to 900 K, we observed the four iron sites A, (Cu(1) chain-site; square planar oxygen coordination with O(5) vacancy on thea-axis), B, (Cu(2) plane-site; square pyramidal oxygen coordination), C, (Cu(1) chain-site; square pyramidal oxygen coordination with O(5) site occupied) and D, (Cu(1) chain-site; quasi-tetrahedral oxygen coordination with O(4) vacancy along theb-axis). At temperatures up to 700 K, the relative area of the B and C sites remained nearly constant as the temperature was increased. However, the area of the A site decreased while, the D site area increased with increasing temperature. At all times, the total area of sites A and D remained constant, thereby indicating the possibility of oxygen atom hopping in thea-b plane. The quadrupole splitting of each site, except the B site, decreased linearly with increasing temperature.
Similar content being viewed by others
References
C. Blue, K. Elgaid, I. Zitkovsky, P. Boolchand, D. McDaniel, W.C.H. Joiner, J. Oostens and W. Huff, Phys. Rev. B37(1988)5905.
P. Boolchand, C. Blue, K. Elgaid, W. Huff, A. Kilinc, D. McDaniel, P. Biswas, D. Zhou and J. Oostens, Hyp. Int. 62(1990)73.
E. Baggio-Saitovitch, R.B. Scorzelli, I. Souza Azevedo and F.J. Litterst, Hyp. Int. 70(1992)1231.
P. Boolchand and D. McDaniel,Studies on High Temperature Superconductors, Vol. 4, ed. A.V. Narlikar (Nova Science Publ., 1990) pp. 143–198.
J.D. Jorgensen, M.A. Beno, D.G. Hinks, L. Soderholm, K.J. Volin, R.L. Hitterman, J.D. Grace, I.K. Schuller, C.U. Segre, K. Zhang and M.S. Kleefisch, Phys. Rev. B36(1987)3608.
Z. Yu, Y. Zhou, X. Jin, Q. Lu, R. Huang, R. Liu and Y. Hsia, Hyp. Int. 55(1990)1411.
M.G. Smith, R.D. Taylor and H. Oesterreicher, Phys. Rev. B42(1990)4202.
Author information
Authors and Affiliations
Additional information
Research supported in part by the Old Dominion University Undergraduate Research Program.
Rights and permissions
About this article
Cite this article
Ford, D.J., Cook, D.C., Gardner, J.A. et al. A high temperature Mössbauer effect study of iron-doped YBa2Cu3O7 superconductor. Hyperfine Interact 93, 1627–1633 (1994). https://doi.org/10.1007/BF02072919
Issue Date:
DOI: https://doi.org/10.1007/BF02072919