Hydrogenolysis of n-butane over Ru/SiO2 catalysts of high ruthenium dispersity

  • D. Nazimek


Ruthenium catalysts Ru/SiO2 were obtained from 2RuOHCl2. 7NH3 solution by means of ion exchange between the OH groups on the SiO2 surface and using classical impregnation from acid RuCl3 solution. The measurement of the rate of n-butane hydrogenolysis was carried out in a gradientless reactor. Measurements were made within the temperature range of 470–670 K at H2∶C4H10 ratio equal to 6∶1. The results obtained indicate a definite influence of the dispersity of ruthenium on the reaction rate of the hydrogenolysis of n-butane and on the selectivity of this process. The effect of the degree of Ru dispersity on the rate of n-butane hydrogenolysis was examined A correlation was found between the dispersity of Ru and the selectivity to methane, ethane and propane.


Methane SiO2 Propane Ethane Ruthenium 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Рутениевые катализаторы Ru/SiO2 были получены из раствора 2RuOHCl2. 7NH3 с помощью ионного обмена с группами OH на поверхности SiO2 и, используя классическое импрегнирование из кислых растворов RuCl3. Измерение скорости гидрогенолиза н-бутана проводилось в реакторе без градиента. Измерения велись в интервале температур 470–670 К при отношении H2∶C4H10, равном 6∶1. Полученные результаты свидетельствуют об определенной зависимости мэжду дисперсностью рутения и скоростью реакции гидрогенолиза н-бутана, а также селективностью этого процесса. Было исследовано влияние степени дисперсности на скорость гидрогенолиза н-бутана. Была найдена корреляция между дисперсностью Ru и селективностью к образованию метана, этана и пропана.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    J. H. Sinfelt: Catal. Rev.3, 175 (1970)Google Scholar
  2. 2.
    C. W. Bragin, A. L. Liberman: Prewraszczenija uglewodorodow na metall-soderschaschich katalitorach, “Chimija”, Moskva 1981Google Scholar
  3. 3.
    D. Nazimek: Fuel (in press)Google Scholar
  4. 4.
    J. Barcicki, D. Nazimek, W. Grzegorczyk, T. Borowiecki, B. Krzywania: Annalec UMCS,36, AA, 169 (1981)Google Scholar
  5. 5.
    T. E. Madey, J. T. Yates, D. R. Sandstrom, R. J. H. Voorhoeve: Treat. on Solid. State Chem.,6B, 1–124 (1964)Google Scholar
  6. 6.
    R. A. Van Hardeveld, A. Van Montfoort: Surf. Sci.,4, 396 (1966)Google Scholar
  7. 7.
    D. Nazimek: Appl. Catal. (in press)Google Scholar
  8. 8.
    J. J. Carberry: Catal. Rev.,3, 61 (1970)Google Scholar
  9. 9.
    J. R. Anderson: Adv. Catal.,23, 1 (1973)Google Scholar
  10. 10.
    G. A. Martin: J. Catal.,60, 345 (1979)Google Scholar
  11. 11.
    A. Sárkány, P. Tétényi: React. Kinet. Catal. Lett.,12, 297 (1979)Google Scholar

Copyright information

© Akadémiai Kiadó 1985

Authors and Affiliations

  • D. Nazimek
    • 1
  1. 1.Department of Chemical Technology, Institute of ChemistryMaria Curie-Sklodowska UniversityLublinPoland

Personalised recommendations