, Volume 48, Issue 1, pp 163–169 | Cite as

Stabilization of hopcalite catalyst in alumina matrix

  • Z. Jaworska-Galas
  • W. Miśta
  • J. Wrzyszcz
  • M. Zawadzki
Article
  • 30 Downloads

Abstract

The properties of hopcalite in alumina matrix have been investigated and compared with conventional hopcalite catalyst. It was found using X-ray diffraction, DTA-TG, TEM, and activity measurements in oxidation of n-butane that the presence of alumina matrix leads to weakening of phase changes of hopcalite and recrystallization of CuMn2O4 spinel. The modified catalyst was also found to show higher activity after calcination at 1073 K than pure hopcalite under the same conditions.

Keywords

Oxidation Alumina Physical Chemistry Catalysis Recrystallization 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Abstract

Свойства гопкалита на алюминиевой матрице исследовали и сравнивали с обычным гопкалитным катализатором. С помощью рентгеновской диффракции, ДТА, ТГ и ТЕМ и измерений активности в окислении н-бутана установили, что присутствие матрицы окиси алюминия приводит к уменьшению фазовых изменений гопкалита и перекристаллизации спинельного CuMn2O4. Так, модифицированный катализатор обладает повышенной активностью после кальцинирования при 1073 K по сравнению с чистым гопкалитом в тех же условиях.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. M. C. Dermott: in “Pollution Control Review”, Vol. 2,8 Noyes Data Corp., Park Ridge, IL, 1971, 1972.Google Scholar
  2. 2.
    S. B. Kanungo: J. Catal.,58, 419 (1979).Google Scholar
  3. 3.
    G. M. Schwab, S. B. Kanungo: Z. Phys. Chem., N. F.,107, 109 (1977).Google Scholar
  4. 4.
    J. Supniewski: in “Preparatyka Organiczna” 620. PWN 1958.Google Scholar
  5. 5.
    J. Wrzyszcz, S. Janiak, Z. Jaworska-Galas: Polish Pat. Appl., P-278321 (1989).Google Scholar
  6. 6.
    idem J. Wrzyszcz, S. Janiak, Z. Jaworska-Galas: Polish Pat. Appl., P-278322 (1989).Google Scholar
  7. 7.
    J. Wrzyszcz, S. Janiak, Z. Jaworska-Galas, S. Kulak: Przem. Chem.,56, 654 (1977).Google Scholar
  8. 8.
    S. Veprek, D. L. Cocke, S. Kehl, H. R. Oswald: J. Catal.,100, 250 (1986).Google Scholar
  9. 9.
    Z. Jaworska-Galas, S. Janiak, W. Miśta, J. Wrzyszcz, M. Zawadzki: J. Mater. Sci. (in press).Google Scholar

Copyright information

© Akadémiai Kiadó 1992

Authors and Affiliations

  • Z. Jaworska-Galas
    • 1
  • W. Miśta
    • 1
  • J. Wrzyszcz
    • 1
  • M. Zawadzki
    • 1
  1. 1.Department of Catalysis, W. Trzebiatowski Institute of Low Temperature and Structure ResearchPolish Academy of SciencesWrocławPoland

Personalised recommendations