Abstract
The influence of subthreshold-energy electrons on the formation and annealing of structural defects in ZnTe and on the annealing of dislocation loops preinjected in the sample by bombardment with argon ions is investigated by transmission electron microscopy. The final form and density of structural defects formed after electron irradiation is observed to depend on the total electron flux, whereas the rate of formation of defects and annealing of dislocation loops increases linearly with the intensity of electron irradiation. A comparison is drawn with CdZnTe, Si, and GaAs irradiated under similar conditions. The results are attributed to subthreshold defect nucleation mechanisms.
Similar content being viewed by others
References
J. W. Corbett and J. C. Bourgoin, in: Point Defects in Solids, Vol. 2, J. H. Crawford and L. M. Slifkin (eds.), Plenum Press, New York (1975).
A. L. Aseev, L. I. Fedina, D. Kheél', and Kh. Barch, Clustering of Interstitial Atoms in Silicon and Germanium [in Russian], Nauka, Novosibirsk (1990).
A. J. Forty, Brit. J. Appl. Phys.,14, 3–9 (1963).
J. H. O. Varley, J. Phys. Chem. Solids,23, 985 (1962).
A. Nouruzi-Khorasani, P. W. Hutchinson, and P. S. Dobson, Radiat. Eff.,55, 79 (1981).
Y. Y. Loginov, P. D. Brown, and N. Thompson, Phys. Stat. Solidi A,126, 63–83 (1991).
G. Lu, F. Niu, and R. Wang, Rad. Eff. Def. Solids,116, 81–94 (1991).
M. H. Loretto, Electron Beam Analysis of Materials, Chapman and Hall, London-New York (1984).
Y. Y. Loginov, P. D. Brown, and N. A. Thompson, Phys. Stat. Solidi A,127, 75–86 (1991).
V. G. Karpov and M. I. Klinger, Fiz. Tekh. Poluprovodn.,12, No. 10, 1887–1897 (1987).
Author information
Authors and Affiliations
Additional information
Translated from Izvestiya Vysshikh Uchebnykh Zavedenii, Fizika, No. 1, pp. 111–115, January, 1996.
Rights and permissions
About this article
Cite this article
Loginov, Y.Y., Lu, G. Electron microscope studies of the influence of electrons with subthreshold energies on the formation and annealing of structural defects in ZnTe and CdZnTe. Russ Phys J 39, 102–106 (1996). https://doi.org/10.1007/BF02069252
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02069252