Structural changes of faujasite—Type zeolites under the influence of sulfur dioxide adsorption

  • M. Ziólek


The X-ray and IR studies of faujasite-type zeolites after sulfur dioxide adsorption showed that in the case of X-type zeolites a partial destruction of the zeolite lattice occurred. The modified X-type zeolites have smaller resistance to the SO2 treatment. No influence of sulfur dioxide on the structure of Y-type zeolites was observed.


Sulfur Physical Chemistry Dioxide Zeolite Catalysis 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Изучение методами рентгенострукурного анализа и ИК-спектроскопии цеолитов типа фауязита после адсорбции двуокиси серы показало, что в случае цеолитов типа Х обработка двуокисью серы оказывает еще большее действие, если цеолиты модифицированы, при зтом наблюдается частичная деструкция решетки. В то же время двуокись серы не оказывает никакого действия на структуру типа У.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    M. Ziólek, Z. Dudzik: React. Kinet. Catal. Lett.,14, 213 (1980).Google Scholar
  2. 2.
    M. Ziólek, Z. Dudzik: React. Kinet. Catal. Lett.,22, 457 (1983).Google Scholar
  3. 3.
    Z. Dudzik, M. Ziólek: J. Catal.,51, 345 (1978).Google Scholar
  4. 4.
    M. Flanigen: ACS Monograph 171, Zeolite Chemistry and Catalysis p. 80, 1976.Google Scholar
  5. 5.
    G. D. Chukin, B. V. Smirnov: Zh. Fiz. Khim.,50, 141 (1976).Google Scholar
  6. 6.
    V. I. Fisak: Probl. Teploenerg. Prikl. Teplofiz., 28 (1979).Google Scholar

Copyright information

© Akadémiai Kiadó 1983

Authors and Affiliations

  • M. Ziólek
    • 1
  1. 1.Laboratory of Zeolite Catalysis, Institute of ChemistryA. Mickiewicz UniversityPoznańPoland

Personalised recommendations