Short-range order in the Fe-B-Sn amorphous system

  • B. Arcondo
  • F. Audebert
  • A. Lorenzo
  • H. Sirkin
Amorphous Materials, Quasicrystals, and Nanocrystalline Materials


Melt quenched FeBSn samples of different compositions were prepared with three different quenching rates and analyzed by Mössbauer spectroscopy and X-ray diffraction. In a previous work, the glass-forming tendency in this system was analyzed, In the present work, the short-range order is studied and an improvement in the determination of the glass-forming composition range is achieved. Mössbauer spectra were fit using hyperfine field distributions.


Spectroscopy Thin Film Field Distribution Composition Range Hyperfine Field 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. [1]
    C.L. Chien, D. Musser, E.M. Gyorgy, R.C. Sherwood, H.S. Chen, F.E. Luborsky and J.L. Walker, Phys. Rev. B20(1979)283.Google Scholar
  2. [2]
    G.L. Whittle, P. Wells, S.J. Campbell, A. Calka and A.M. Stewart,Rapidly Quenched Metals, Vol. 1, eds. S. Steeb and H. Warlimont (North-Holland, Amsterdam, 1984) p. 545.Google Scholar
  3. [3]
    N. Cowlam and G.E. Carr, J. Phys. F15(1985)1109.Google Scholar
  4. [4]
    Ph. Mangin and G. Marchal, Phys. Lett. A68(1978)466.Google Scholar
  5. [5]
    G. Marchal, Ph. Mangin, M. Piecuch, B. Rodmacq and Chr. Janot, Mater. Sci. Eng. 36(1978)11.Google Scholar
  6. [6]
    B. Rodmacq, M. Piecuch, G. Marchal, Ph. Mangin and Chr. Janot, IEEE Trans. Magn. 14(1978)841.Google Scholar
  7. [7]
    B. Rodmacq, M. Piecuch, Chr. Janot, G. Marchal and Ph. Mangin, Phys. Rev. B21(1980)1911.Google Scholar
  8. [8]
    R.A. Dunlap, J. Phys. F14(1984)549.Google Scholar
  9. [9]
    R.A. Dunlap, Solid State Commun. 43(1982)57.Google Scholar
  10. [10]
    L. Battezzati, C. Antonione and G. Riontino, J. Non-Cryst. Solids 89(1987)114.Google Scholar
  11. [11]
    B. Arcondo, A. Lorenzo, F. Audebert and H. Sirkin,LACAME'92, Hyp. Int. 83(1994)281.Google Scholar
  12. [12]
    R.A. Brand, 1987Normos Programs, Internal Report, Angewandte Physik, Universität Duisburg.Google Scholar
  13. [13]
    R.A. Brand, J. Lauer and D.M. Herlach, J. Phys. F13(1983)675.Google Scholar
  14. [14]
    L. Billard and A. Chamberod, Solid State Commun. 17(1975)113.Google Scholar
  15. [15]
    J. Hesse, J.B. Müller and B. Weichman, J. de Phys. 40(1979)C2–161.Google Scholar

Copyright information

© J.C. Baltzer AG, Science Publishers 1994

Authors and Affiliations

  • B. Arcondo
    • 1
  • F. Audebert
    • 1
  • A. Lorenzo
    • 1
  • H. Sirkin
    • 1
  1. 1.Departamento de Física, Facultad de IngenieriaUniversidad de Buenos AiresBuenos AiresArgentina

Personalised recommendations