Abstract
The effects of surface dehydration on textural properties, crystallinity and the structure of AlPO4−ZrO2 (weight ratio AlPO4/ZrO2=3) systems precipitated with ethylene oxide have been studied by N2 adsorption and XRD measurements. The increase in calcination temperature in the range 773–1273 K decreases the textural parameters as a consequence of AlPO4 crystallization to the tridymite form.
Abstract
Влияние дегидрирования поверхности на текстурные свойства, кристалличность и структуру систем AlPO4−ZrO2 (весовое соотношение AlPO4/ZrO2=3), высажденных окисью этилена, исследовали адсорбцией N2 и рентгено-дифракционными измерениями. Увеличение температуры обжига от 773 до 1273 К уменьшает текстурные параметры, что является следствием кристаллизации AlPO4 в тридимитную форму.
Similar content being viewed by others
References
J. B. Moffat: Catal. Rev. Sci. Eng.,18, 199 (1978).
J. M. Campelo, A. Garcia, D. Luna, J. M. Marinas: J. Catal.,102, 299 (1986).
J. M. Campelo, A. Garcia, D. Luna, J. M. Marinas: J. Catal., in press.
A. Blanco, J. M. Campelo, A. Garcia, D. Luna, J. M. Marinas: React. Kinet. Catal. Lett., submitted for publication
A. Blanco, J. M. Campelo, A. Garcia, D. Luna, J. M. Marinas: React. Kinet. Catal. Lett., submitted for publication
S. Brunauer, R. Sh. Mikhail, E. Bodor: J. Colloid Interface Sci.,24, 541 (1967).
S. Brunauer, L. S. Deming, W. S. Deming, E. Teller: J. Am. Chem. Soc.,62, 1723 (1940).
A. Lecloux, J. P. Pirard: J. Colloid Interface Sci.,70, 265 (1979).
A. Blanco, J. M. Campelo, A. Garcia, D. Luna, J. M. Marinas: Appl. Catal., in press.
O. W. Florke: Zeit. Kristallogr.,125, 134 (1967).
V. R. Cypres, R. Wollast, J. Rancq: Ber. Dtsch. Keram. Ges.,40, 527 (1963).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Blanco, A., Campelo, J.M., Garcia, A. et al. AlPO4−ZrO2 catalysts, II. Synthesis, textural properties and crystal structure of systems obtained in ethylene oxide. React Kinet Catal Lett 38, 223–228 (1989). https://doi.org/10.1007/BF02062110
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02062110