Influence of silica on the phase composition of vanadium-molybdenum oxide catalysts

  • T. P. Gorshkova
  • D. V. Tarasova
  • I. P. Olenkova
  • N. G. Maksimov
  • V. F. Anufrienko
Article

Abstract

The presence of silica inhibits the formation of V2MoO8 during thermal treatment of vanadium-molybdenum oxide catalysts in air. In its presence, vanadium-molybdenum compounds are formed under reductive conditions.

Keywords

Oxide Physical Chemistry Catalysis Phase Composition Thermal Treatment 

Abstract

При термообработке на воздухе окисных ванадий-молибденовых катализаторов наличие силикагеля препятствует образованию соединения V2MoO8. В присутствии силикагеля окисные ванадий-молибденовые соединения образуются в восстановвительных условиях.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    L. M. Plyasova, G. A. Zenkovets, I. P. Olenkova, D. V. Tarasova: Izv. Sib. Otd. Akad. Nauk SSSR, Ser. Khim. Nauk (in press).Google Scholar
  2. 2.
    G. E. Selyutin, N. G. Maksimov, G. A. Zenkovets, D. V. Tarasova, V. F. A. Anufrienko: React. Kinet. Catal. Lett.,10, 25 (1979).Google Scholar
  3. 3.
    V. B. Kazanskii: Problemy Kinetiki i Kataliza,15, 77, Nauka, Moskva 1973.Google Scholar
  4. 4.
    T. N. Kuznetsova, T. V. Andrushkevich, G. K. Boreskov, L. M. Plyasova, N. G. Maksimov: React. Kinet. Catal. Lett.,12, 531 (1979).Google Scholar
  5. 5.
    Yu. D. Tretyakov: Tverdofaznye Reaktsii. Nauka, Moskva 1978.Google Scholar

Copyright information

© Akadémiai Kiadó 1979

Authors and Affiliations

  • T. P. Gorshkova
    • 1
  • D. V. Tarasova
    • 1
  • I. P. Olenkova
    • 1
  • N. G. Maksimov
    • 1
  • V. F. Anufrienko
    • 1
  1. 1.Institute of CatalysisNovosibirskUSSR

Personalised recommendations