Carbon content and H₂ chemisorption of a regenerated Pt catalyst

Abstract

The effect of the cracking of¹⁴C-labelled cyclohexene on the chemisorption (thermodesorption) of hydrogen on a thermally treated Pt powder catalyst has been studied. It has been established that (i) under the usual conditions of regeneration (calcination of the catalyst at 500°C for 1–2 hrs in a stream of air) the products of cracking cannot be completely removed from the catalyst, and (ii) as compared with the pure catalyst, the carbon deposit content of the catalyst not only increases the amount of chemisorbed hydrogen but also leads to new desorption peaks on the thermodesorption curve.

Abstract

Был исследован эффект крекинга циклогексана, меченного C¹⁴, на хемисорбцию (термодесорбцию) водорода на катализаторе термообработанного порошка платины. Было найдено что (1) в обычных условиях процесса регенерации (нагревание катализатора при 500°C в течение 1–2 часов в потоке воздуха) продукты крекинга могут быть полностью удалены с катализатора и (2) присутствие углеродного насадка на катализаторе-по сравнению с чистым катализатором-приводит не только к увеличению количества хемисорбированного водорода, но также и к изменению характеристик термодесорбционной кривой: появлению новых пиков десовбции.