  • T. Rentschler
  • U. Sazama
Inorganic and Coordination Chemistry
  • 24 Downloads

Abstract

The reversible cycling of the oxygen content in layered Co-substituted perovskites of type YBaFeCuO5+δ was investigated applying thermoanalytical methods. For the system YBaCoCu1−xFexO5+δ an increasing amount of oxygen incorporation into the oxygen deficient lattice was found by thermogravimetry for an increasing iron content ofx=0.4 to 0.8. With a cycle of subsequent heating and cooling the reversible incorporation of oxygen on account of redox active cations with mixed valencies could be demonstrated. The combination of several cycles under different gas atmospheres confirmed the reversibility of the oxidation processes suggesting the application for catalytical processes.

Keywords

perovskite reversible oxygen incorporation thermal reactivity thermogravimetry 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    A.W. Mombru, C. Christides, A. Lappas, K. Prassides, M. Pissas, C. Mitros and D. Niarchos, Inorg. Chem., 33 (1994) 1255.CrossRefGoogle Scholar
  2. 2.
    V. Caignaert, I. Mirebeau, F. Bourée, N. Nguyen, A. Ducouret, J.-M. Grenche and B. Raveau, J. Solid State Chem., 114 (1995) 24.CrossRefGoogle Scholar
  3. 3.
    T. Rentschler, J. Alloys Comp., 232 (1996) 43.CrossRefGoogle Scholar
  4. 4.
    T. Rentschler, Thermochim. Acta, in press.Google Scholar
  5. 5.
    L. Barbey, N. Nguyen, A. Ducouret, V. Caignaert, J.M. Grenche and B. Raveau, J. Solid State Chem., 115 (1995) 514.CrossRefGoogle Scholar

Copyright information

© Akadémiai Kiadó 1996

Authors and Affiliations

  • T. Rentschler
    • 1
  • U. Sazama
    • 1
  1. 1.Institute of Inorganic and Applied ChemistryUniversity of HamburgHamburgGermany

Personalised recommendations