Abstract
TG, DSC and X-ray measurements were made to characterize the water absorption process by Li (50%) — Na (50%)β-alumina.
The equilibrium water content, dehydration enthalpies and lattice parameter values have been determined and compared with those previously obtained for pure Li and Naβ-aluminas.
The mixedβ-alumina is shown to be very similar to Liβ-alumina as concerns the dehydration enthalpy and the temperature range in which the dehydration occurs, while it seems to be very similar to Naβ-alumina with respect to the equilibrium water content andc-axis values.
Zusammenfassung
Zur Charackterisierung des Wasseradsorptionsprozesses an Li(50%)-Na(50%)β-Aluminiumoxid wurden TG-, DSC- und Röntgendiffraktionsmessungen ausgeführt. Der Gleichgewichtswassergehalt, die Dehydratisierungsenthalpien und die Gitterparameter wurden bestimmt und mit denen früher für reines Li- und Na-β-Aluminiumoxid erhaltenen Werten verglichen. Was die Dehydratisierungsenthalpie und den Temperaturbereich der Dehydratisierung betrifft, so verhält sich das gemischteβ-Aluminiumoxid sehr ähnlich dem Li-β-Aluminiumoxid, während es hinsichtlich des Gleichgewichtswassergehaltes und der Gitterkonstantec dem Na-β-Aluminiumoxid sehr nahe steht.
Резюме
С целью определения п роцесса поглощения в оды смешанным Li(50%) — Na(50%)β-алюмином, проведены его ТГ, ДСК и рентгенографически е исследования. Опред елено равновесное содержа ние воды, значение энт альпии дегидратации и парам етр решетки. Полученные результа ты сопоставлены с ран ее полученными для чист ых Li и Naβ-алюминов. Относительно энталь пии дегидратации и те мпературной области, в которой про исходит дегидратация, смешан ныйβ-алюмина подобе н чистому Liβ-алюмину. Значения р авновесного qsодержания воды и вели чина постоянной реше тки вдоль с-кристаллогра фической оси для смешанного алюми на подобны чистому Naβ-алюмину.
Similar content being viewed by others
References
G. A. Rankin and H. E. Merwin, J. Am. Chem. Soc., 38 (1916) 568.
R. Ridgway, A. Klein and W. O'Leary, Trans. Electrochem. Soc., 70 (1936) 71.
Y. F. Y. Yao and J. T. Kummer, J. Inorg. Nucl. Chem., 29 (1967) 2453.
J. T. Kummer, Prog. in Solid State Chem., 7 (1972) 141.
D. Kline, H. S. Story and W. L. Roth, J. Chem. Phys., 57 (1972) 5180.
J. B. Bates, R. French, H. Engstrom, J. C. Wang and T. Kaneda, Solid State Ionics, 1, (1980) 15.
L. M. Foster, Fast Ion Transport in Solids Electrodes and Electrolytes, North Holland, Amsterdam, 1979, p. 249.
R. D. Armstrong, P. M. A. Sherwood and R. A. Wiggins, Spectrochim. Acta, 30A (1974) 1213.
G. Flor, A. Marini, V. Massarotti and M. Villa, Solid State Ionics, 2 (1981) 195.
V. Massarotti, G. Campari-Viganó, G. Flor and A. Marini, J. Appl. Cryst., 15 (1982) 471.
A. Marini, G. Flor, V. Massarotti, A. R. McGhie and G. C. Farrington, to be published.
G. Spinolo, V. Massarotti and G. Campari, J. Phys. E.: Sci. Instr., 12 (1979) 1059.
C. R. Peters, M. Bettman, J. W. Moore and M. D. Glick, Acta Cryst., B 27 (1971) 1826.
A. J. C. Wilson, Mathematical Theory of X-ray powder diffractometry. Philips, Eindhoven, 1963.
J. C. Wang, J. B. Bates, T. Kaneda, H. Engstrom, D. F. Pickett and Sang-II Choi, Fast Ion Transport in Solids Electrodes and Electrolytes, North Holland, Amsterdam, 1979, p. 379.
Author information
Authors and Affiliations
Additional information
Was supported by MPI fondi 40%.
Rights and permissions
About this article
Cite this article
Marini, A., Flor, G., Massarotti, V. et al. β-Aluminas and water. Journal of Thermal Analysis 28, 303–309 (1983). https://doi.org/10.1007/BF01983264
Issue Date:
DOI: https://doi.org/10.1007/BF01983264