, Volume 38, Issue 9, pp 2129–2135 | Cite as

Simultaneous thermal analyses for thermal dissociation studies on ZrO2

  • M. Szalkowicz
Inorganic Substances
  • 24 Downloads

Abstract

The behaviour of zirconium oxide ZrO2 during its heating in the temperature range 300–2670 K under high-vacuum conditions and at different heating rates has been studied.

The experiments were performed with a Swiss made Universal Mettler thermoanalyser equipped with a super-high-temperature furnace SHT. Volatile products were analyzed simultaneously by means of a Balzers QMG-101 mass spectrometer.

An analysis of the TG, DTG, DTA and EGA curves recorded simultaneously has shown the complex character of the studied process. The elementary steps of the overall process were defined and taken into consideration. The mechanism of the thermal dissociation reaction of ZrO2 as function of the hearing rate was discussed too.

Keywords

kinetics thermal dissociation ZrO2 

Zusammenfassung

Im Temperaturintervall von 300 K bis 2670 K wurde im Hochvakuum und bei verschiedenen Aufheizgeschwindigkeiten das thermische Verhalten von Zirkoniumoxid ZrO2 untersucht.

Die Experimente wurden mit Hilfe eines schweizer Universal Mettler Thermoanalysators, ausgerüstet mit einem SHT Super-Hochtemperatur-Ofen, ausgeführt. Flüchtige Produkte wurden simultan dazu mit einem Massenspektrometer QMG-101 der Balzers-Company analysiert.

Die Auswertung der durch aufgezeichneten TG-, DTG-, DTA- und EGA-Kurven zeigt den komplexen Charakter des untersuchten Prozesses. Die Elementarschritte der Gesamtreaktion wurden definiert und berücksichtigt. Weiterhin wurde der Mechanismus der Thermodissoziation von ZrO2 auch in Abhängigkeit von der Aufheizgeschwindigkeit diskutiert.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Setaram-France, Thermal analysis at high and very high temperature, B/14DOCCOMA, 1991, p. 31.Google Scholar
  2. 2.
    I. S. Kulikov, Processy vostanovlenia i plavlenia Fe, Mockow 1982, p. 23.Google Scholar
  3. 3.
    R. C. Mackenzie and G. Berggren, Differential Thermal Analysis, R. C. Mackenzie Ed., Vol. 1., London-New York 1970, p. 196.Google Scholar
  4. 4.
    G. Pilojan, I. Rasonskaia and O. Novikova, Mat. Vsesouznovo Symp. po metod. voprosom termicheskovo analysa. Izd. Kazanskovo Universyteta, Kazan 1968, p. 35.Google Scholar
  5. 5.
    Z. Kubas and M. Szalkowicz, Thermal Analysis. Proc. Third ICTA Vol. 2, Davos 1972, p. 447.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1992

Authors and Affiliations

  • M. Szalkowicz
    • 1
  1. 1.Institute of Iron Metallurgy, Department of Physical ChemistryAcademy of Mining and MetallurgyKrakówPoland

Personalised recommendations