Journal of thermal analysis

, Volume 37, Issue 5, pp 1015–1023

Kinetics of thermal decomposition of metal acetates

  • M. Afzal
  • P. K Butt
  • H. Ahmad
Article

Abstract

The acetates of magnesium, nickel, copper, manganese, sodium and barium were subjected to thermal decomposition by means of thermogravimetric techniques (TG) under a constant flow of nitrogen. The decompositions occurred in steps and the kinetics of every set of reactions was determined by the Coats and Redfern method. These results were analysed to establish the decomposition kinetics and hence to calculate activation energies. The activation energies were also determined by applying the Horowitz-Hugh method, which yielded similar results.

Zusammenfassung

Mittels TG in konstantem Stickstoffstrom wurde die thermische Zersetzung von Magnesium-, Nickel-, Kupfer-, Mangan-, Natrium- und Bariumazetat untersucht. Es erfolgte eine schrittweise Zersetzung, die Kinetik für jede der Reaktionen wurde mit Hilfe der Methode von Coats und Redfern bestimmt. Diese Ergebnisse wurden genutzt, um die Kinetik der Zersetzung und anschlie\end die Aktivierungsenergien festzustellen. Ähnliche Werte für die Aktivierungsenergien erhielt man auch mit Hilfe der Methode von Horowitz Hugh.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    K. C. Patel, G. V. Chandrashekhar, M. V. George and C. N. R. Rao, Canad. J. Chem., 46 (1968) 257.Google Scholar
  2. 2.
    C. Dual, Anal. Chim. Acta, 13 (1955) 32.Google Scholar
  3. 3.
    M. A. Bernard and F. Busnot, Bull. Soc. Chim. Fr., 5 (1968) 2000.Google Scholar
  4. 4.
    C. Dual, Anal. Chim. Acta, 20 (1959) 264.Google Scholar
  5. 5.
    L. Walter-Leavy and J. Laniepce, Comp. Rend., 250 (1960) 332.Google Scholar
  6. 6.
    D. R. Glasson, J. Appl. Chem., 13 (1963) 124.Google Scholar
  7. 7.
    M. D. Judd, B. A. Plunkett and M. I. Pope, J. Thermal Anal., 6 (1974) 555.Google Scholar
  8. 8.
    D. W. Kureben, D. W. van Heerden, C. Van and F. J. Huntjens, Fuel, 30 (1951) 253.Google Scholar
  9. 9.
    E. S. Freeman and B. Carroll, J. Phys. Chem., 62 (1968) 394.Google Scholar
  10. 10.
    C. D. Doyle, J. Appl. Polymer Sci., 5 (1961) 285.Google Scholar
  11. 11.
    H. H. Horowitz and G. Metzger, Anal. Chem, 35 (1963) 1464.Google Scholar
  12. 12.
    A. W. Coats and J. P. Redfern, Nature, 201 (1964) 68.Google Scholar
  13. 13.
    F. Burriel-Marti, S. Jiminez-Gomes and C. Altwarez-Herrero, An. Edafol. Fissiol. Veg., 14 (1955) 221.Google Scholar
  14. 14.
    A. E. Newtek, Thermochim. Acta, 2 (1971) 1.Google Scholar
  15. 15.
    W. R. Pease, R. L. Segall, R. St. C. Smart and P. S. Turner, J. Chem. Soc. Faraday Trans., 82 (1982) 747.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1991

Authors and Affiliations

  • M. Afzal
    • 1
  • P. K Butt
    • 1
  • H. Ahmad
    • 1
  1. 1.Department of ChemistryQuaid-I-Azam UniversityIslamabadPakistan

Personalised recommendations