Thermal dissociation of basic aluminium ammonium sulfate in vacuum

Part II. Kinetics of the process
  • J. Pysiak
  • Barbara Pacewska
Article

Abstract

Investigations were carried out on the kinetics of thermal decomposition of basic aluminium ammonium sulfate in vacuum. The kinetic model of dissociation of the compound was identified. The results of the kinetic studies and the mechanism of the process are discussed.

Keywords

Polymer Aluminium Sulfate Ammonium Physical Chemistry 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Résumé

La cinétique de la décomposition thermique sous vide du sulfate basique d'aluminium et d'ammonium a été étudiée. On a identifié les paramètres du modèle cinétique de la dissociation de ce composé. Les résultats des études cinétiques et le mécanisme du processus de décomposition sont discutés.

Zusammenfassung

Es wurde die Kinetik der thermischen Zersetzung von basischem Ammoniumaluminiumsulfat im Vakuum untersucht. Die Parameter für das kinetische Modell der Dissoziation von der Verbindung wurden identifiziert und die Ergebnisse der kinetischen Untersuchungen im Zusammenhang mit dem Verfahrensmechanismus besprochen.

Резюме

Исследована в вакуум е кинетика термическ ого разложения основног о сульфата алюминия - аммония. Опр еделены кинетически е параметры всех стадий процесса и установлена математ ическая модель терми ческого разложения соединен ия в соответствии с механизмом процесс а.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    St. Bretsznajder andJ. Pysiak, Bull. Acad. Polon. Sci. Ser. Chim., 12 (1964) 315.Google Scholar
  2. 2.
    St. Bretsznajder andJ. Pysiak, Bull. Acad. Polon. Sci. Ser. Chim., 12 (1964) 201.Google Scholar
  3. 3.
    St. Bretsznajder andJ. Pysiak, Chem. Stosowana, 2A (1965) 137.Google Scholar
  4. 4.
    P. J. Pizzolato andH. A. Papazian, J. Am. Ceram. Soc., 53 (1970) 289.Google Scholar
  5. 5.
    H. A. Papazian, P. J. Pizzolato andR. R. Orrel, Termochim. Acta, 4 (1972) 97.Google Scholar
  6. 6.
    D. W. Johnson, Jr. andP. K. Gallagher, J. Am. Ceram. Soc., 54 (1971) 461.Google Scholar
  7. 7.
    D. W. Johnson, Jr. andP. K. Gallagher, J. Phys. Chem., 76 (1972) 1474.CrossRefGoogle Scholar
  8. 8.
    D. W. Johnson, Jr. andP. K. Gallagher, Thermochim. Acta, 6 (1974) 333.CrossRefGoogle Scholar
  9. 9.
    H. Papazian, P. J. Pizzolato andR. R. Orrel, Thermochim. Acta, 6 (1973) 337.CrossRefGoogle Scholar
  10. 10.
    N. A. Warner andT. R. Ingraham, Can. J. Chem. Eng., 40 (1962) 263.Google Scholar
  11. 11.
    J.Pysiak and B.Pacewska, J. Thermal. Anal., (in print).Google Scholar
  12. 12.
    J. Pysiak, B. Podlaska andR. Marcinkowski, Roczniki Chem., 47 (1973) 133.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1980

Authors and Affiliations

  • J. Pysiak
    • 1
  • Barbara Pacewska
    • 1
  1. 1.Institute of ChemistryWarsaw Technical University, Branch at PłockPoland

Personalised recommendations