Etude calorimetrique de l'enthalpie de dissolution d'alumines industrielles dans des bains cryolithiques

  • M. Yagoubi
  • Y. Bertaud
  • R. Castanet
Article

Abstract

The partial molar enthalpies of dissolution in cryolitic baths of two different industrial aluminas were measured by calorimetry at 1290 K. The influence of the physico-chemical properties of the aluminas and of additions of excess AlF3 in the bath were examined.

The effects of the presence in the solvent of NaF and LiF (F donors) and of AlF3 in excess (F acceptor) agree well with the proposed mechanism of dissolution of alumina in cryolite.

Zusammenfassung

Mittels Kalorimetrie wurden die partiellen molaren Lösungsenthalpien bei 1290 K für zwei verschiedene industrielle Tonerden in Kryolith-Bädern bestimmt. Der Einfluß der physikalischen Eigenschaften der Tonerden und des Zusatzes von AlF3 im Überschluß wurde untersucht. Die durch die Gegenwart von NaF, LiF (F-Donoren) bzw. überschüssigem AlF3 (F-Akzeptor) im Bad verursachten Effekte stimmen gut mit dem für die Lösung von Tonerde in Kryolith vorgeschlagenem Mechanismus überein.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Bibliographie

  1. 1.
    D. Phan-Xuan, R. Castanet et M. Laffitte, Rev. Inter. Htes Temp. et Refract., 11 (1974) 125.Google Scholar
  2. 2.
    D. Phan-Xuan, R. Castanet et M. Laffitte, Rev. Inter. Htes Temp. et Refract., 11 (1974) 285.Google Scholar
  3. 3.
    M. Yagoubi, J-P. Dubès, Y. Bertaud et R. Castanet, J. Therm. Anal., 31 (1986) 1359.Google Scholar
  4. 4.
    T. Kang et R. Castanet, J. Less-Comm. Met., 51 (1977) 125.Google Scholar
  5. 5.
    R. Hultgren, P. D. Desai, D. T. Hawkins, M. Gleiser, K. K. Kelley, et D. D. Wagmans, “Selected values of the Thermodynamic Properties of the Elements”. Amer. Soc. for Metals, Metals Park, Ohio (USA), 1973.Google Scholar
  6. 6.
    P. A. Foster Jr., J. Amer. Cer. Soc., 43 (1960) 66.Google Scholar
  7. 7.
    K. Grojtheim, Norske Videvstas Selslabs Striffev n∘ 5,1956.Google Scholar
  8. 8.
    D. Phan-Xuan, Thèse Sci. Phys., Univ. Aix-Marseille, 1974.Google Scholar
  9. 9.
    W. B. Franck et L. M. Foster Jr., J. Electrochem. Soc., 107 (1960) 997.Google Scholar
  10. 10.
    G. Petit et M. Bourlange, C. R. Acad. Sci. Paris, 270C (1970) 937.Google Scholar
  11. 11.
    K. Halvor, Electrochim. Acta, 25 (1980) 237.Google Scholar

Copyright information

© Wiley Heyden Ltd, Chichester and Akadémiai Kiadó, Budapest 1990

Authors and Affiliations

  • M. Yagoubi
    • 1
  • Y. Bertaud
    • 2
  • R. Castanet
    • 1
  1. 1.Centre de Thermodynamique et de Microcalorimetrie du CNRSMarseille
  2. 2.Laboratoire de Recherches des Fabrications, Aluminium-PechineySt Jean de MaurienneFrance

Personalised recommendations