Oxidative stability of lubricants for dry circuit sliding contacts

  • K. I. Papathomas
  • A. D. Katnani
Article

Abstract

The thin film oxidation resistance of isoparaffin and two polyol esters synthetic lubricants was studied by high pressure differential scanning calorimetry. The oxidation induction time of each lubricant was measured by isothermally heating the sample in an oxygen environment. Arrhenius plots were constructed to predict the service life of the lubricant at low temperatures. The results indicate that polyol esters exhibit better oxidative stability than isoparaffins.

Keywords

Differential Scanning Calorimetry Film Oxidation Polyol Oxidative Stability Oxidation Resistance 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Zusammenfassung

Mittels Hochdruck-Differential-Scanning-Kalorimetrie wurde die Dünnschicht-Oxydationswiderstandsfestigkeit von Isoparaffin- und zwei synthetischen Polyolesterschmiermitteln untersucht. Die Oxydationsinduktionszeit jedes Schmiermittels wurde durch isothermes Erhitzen der Probe in Sauerstoff gemessen. Zur Vorhersage der Lebensdauer der Schmiermittel bei niedrigen Temperaturen wurden die entsprechenden Arrhenius-Diagramme erstellt. Die Ergebnisse zeigen, dass Polyolester über eine bessere oxydative Stabilität verfügen als Isoparaffine.

Резюме

Методом дифференциа льной сканирующей калориметрии высоко го давления изучена устойчивост ь к окислению тонких п ленок изопарафина и двух сл ожных эфиров полиспирта, как синте тических смазок. Инду кционное время окисления кажд ой смазки было измерено путем изоте рмического нагрева о бразца в атмосфере кислорода. Для установления срока службы каждой с мазки при низких темп ературах были построены аррен иусовские графики. Результаты п оказали, что сложные з фиры полиспиртов более ус тойчивы и окислению, чем изопарафины.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    R. V. Steenstrup, V. M. Fiacco and L. K. Schultz, Proceedings of the Twenty-Eighth Annual Holm Conference on Electrical Contacts, 1982 p 59– 68.Google Scholar
  2. 2.
    J. P. Coates and L. C. Setti, ASLE Trans., 29 (3) (1985) 394.Google Scholar
  3. 3.
    J. R. Barcelo and C. Otero, J. Inst. Pet., 50 (1964) 15.Google Scholar
  4. 4.
    A. Zeman, R. Stuwe and K. Koch, Thermochim. Acta, 80 (1984) 1.CrossRefGoogle Scholar
  5. 5.
    E. Dimiroff, J. V. Moffitt and R. D. Quillian, ASME Trans., J. Lubr. Techn., (1969) 406.Google Scholar
  6. 6.
    D. T. Rogers, W. W. Rice and F. L. Jonach, SAE Trans., 64 (1956) 782.Google Scholar
  7. 7.
    J. F. Ford, J. Inst. Pet., 54 (1967) 198.Google Scholar
  8. 8.
    J. A. Walker and W. Tsang, Nat. Bur. Stand. (U.S.), Spec. Publ., 584 (1980) 271.Google Scholar

Copyright information

© Wiley Heyden Ltd, Chichester and Akadémiai Kiadó, Budapest 1988

Authors and Affiliations

  • K. I. Papathomas
    • 1
  • A. D. Katnani
    • 1
  1. 1.IBM CorporationEndicottUSA

Personalised recommendations