Iron(III) oxide formed by decomposition of sodium jarosite as a raw material for ceramic pigments of spinel type

  • Z. Šolc
  • M. Sedlák
  • J. Mracek
Article

Abstract

Iron(III) oxide prepared by the prefiring of jarosite compounds is used for the synthesis of spinel pigments, e.g. ZnFe1−xCr1+xO4. The reactivity of this iron(III) oxide towards zinc oxide decreases as the temperature and duration of the precalcination are increased. The conditions of jarosite compound decomposition significantly influence the colour of the ceramic pigment of Zn-Fe-Cr type too. As concerns the processing of jarosites for the production of H2SO4 and Fe2O3, the optimal conditions of their thermal decomposition are determined.

Keywords

Iron Fe2O3 H2SO4 Thermal Decomposition Eisen 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Zusammenfassung

Mittels Vorbrennen von Jarositverbindungen erhaltenes Eisen(III)-oxid wird zur Herstellung von Spinellpigmenten, z.B. von ZnFe1-xCn+xO4 verwendet. Die Reaktivität dieses Eisen (III)-oxides in der Reaktion mit Zinkoxid nimmt mit steigender Temperatur und Länge der Präkalzinierung ab. Die Bedingungen, unter denen die Zersetzung der Jarositverbindung stattfindet, bestimmen auch eindeutig den Farbton des Keramikpigmentes vom Typ Zn-Fe-Cr. Was die Verwendung dieser Jarosite für die Produktion von H2SO4 und Fe2O3 betrifft, wurden die optimalen Bedingungen für die Zersetzung ermittelt.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    V. Reichert, Proc. of Symposium Progressive Methods of Processing of Concentrated Polymetallic Ores, Jesenik, 1979, p. 117.Google Scholar
  2. 2.
    Z. Šolc and M. Trojan, Proc. Kommunikaty IV. Krajowe Seminarium im. St. Bretsznajdera, Plock, 1986, p. 15.Google Scholar
  3. 3.
    Z. Šolc, M. Trojan, D. Brandová and M. Kuchler, J. Thermal Anal., 33 (1988) 463.Google Scholar
  4. 4.
    Z. Šolc, M. Trojan and J. Jína, Thermanal 1988, Proc. p. B-28.Google Scholar
  5. 5.
    Z. Šolc, V. Balek, M. Trojan and M. Smíd, Thermanal, 1988, Proc. p. A-21.Google Scholar
  6. 6.
    J. Šubrt, T. Hanzlík, A. Solcová and V. Zapletal, Chem. prumysl, 36/61 (1986) 637.Google Scholar
  7. 7.
    B. Pacewska and J. Physiak, J. Thermal Anal., 33 (1988) 511.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1990

Authors and Affiliations

  • Z. Šolc
    • 1
  • M. Sedlák
    • 1
    • 2
  • J. Mracek
    • 1
  1. 1.Institute of Chemical TechnologyPardubiceCzechoslovakia
  2. 2.Factory in BruntálRudné Doly JeseníkCzechoslovakia

Personalised recommendations