Mössbauer studies of thermal decomposition of metal(III) hexacyanoferrates(II)

  • A. S. Brar
  • H. Singh
  • S. Brar
  • B. S. Randhawa
Article

Abstract

The thermal decomposition of metal(III) hexacyanoferrates(II) (Al, As, Sb, Bi) was studied up to 700° in air by employing Mössbauer, infrared spectroscopy and thermal analysis techniques. With the exception of the bismuth compound, the isomer shift of these hexacyanoferrates(II) increases on dehydration at 200°. Dehydration is complete at 200°, decomposition into the ferrite at 300°, and formation ofα-Fe2O3 from aluminium and bismuth hexacyanoferrates(II) and Fe3O4 from antimony and arsenic hexacyanoferrates(II) at 700°.

Keywords

Polymer Aluminium Spectroscopy Ferrite Inorganic Chemistry 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Résumé

On a étudié dans l'air jusqu'à 700°, la décomposition thermique des ferrocyanures de métaux trivalents (Al, As, Sb, Bi), par spectroscopies Mössbauer et infrarouge, ainsi que par les techniques d'analyse thermique. Le déplacement des isomères de ces ferrocyanures augmente lors de la déshydratation à 200°, à l'exception du bismuth. La déshydratation est complète à 200°, la décomposition en ferrite à 300°, la formation d'α-Fe2O3 à partir des ferrocyanures d'aluminium et de bismuth ainsi que du Fe3O4 à partir des ferrocyanures de l'antimoine et de l'arsenic à 700°

Zusammenfassung

Die thermische Zersetzung von Metall(III)ferrocyaniden (Al, As, Sb, Bi) wurde bis zu 700° in Luft unter Anwendung der Mössbauer und Infrarotspektroskopie, sowie thermoanalytischer Techniken untersucht. Die Isomerverschiebung dieser Ferrocyanide nimmt mit der Dehydratisierung bei 200° zu, mit Ausnahme des Wismuts. Die Dehydratisierung ist bei 200° abgeschlossen, die Zersetzung zum Ferrit bei 300° und die Bildung vonα-Fe2O3 aus Aluminium- und Wismutferrocyanid, von Fe3O4 aus Antimon- und Arsenferrocyanid bei 700°.

Резюме

Используя мессбауэр овскую-, ИК спектроско пию и методы термическог о анализа, изучено термическое разложение ферроциа нидов тнехвалентных метал лов — Al, As, Sb, Bi-до температуры 700° в ат мосфере воздуха. Изом ерный сдвиг в ряду ферроциа нидов, за исключением соли в исмута, увеличиваетс я при температуре дегидра тации 200°. Дегидратация происх одят полностью при те мпературе 200°, а при 300° ферроцианид ы алюминия и висмута ра злагаются до феррито в иα-Fe2O3. Ферроцианиды сурьмы и мышьяка разлагаются при 700° с об разованием Fe3O4.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    G. B. Seifer, Zh. Neorgan Khim., 7 (1962) 482, 2219, 1242; 5 (1960) 68.Google Scholar
  2. 2.
    G. B. Seifer andZ. A. Makarove, Zh. Neorgan. Khim., 9 (1964) 2085; 10 (1965) 1022; 11 (1966) 1056.Google Scholar
  3. 3.
    G. B. Seifer andZ. A. Makarove, Dokl. Akad. Nauk, SSSR, 169 (1966) 358.Google Scholar
  4. 4.
    A. E. Greene andM. M. Chamberlain, J. Inorg. Nucl. Chem., 25 (1963) 1471.Google Scholar
  5. 5.
    W. Wolski andB. Porawski, J. Thermal Anal., 9 (1976) 181; 7 (1975) 139.Google Scholar
  6. 6.
    W.Wolski and K.Swiatlak, Russian J. Inorg. Chem. 7 (1971); Zh. Neorg. Khim. 16/7 (1954); Russian J. Inorg. Chem., 22/10 (1977).Google Scholar
  7. 7.
    A. S. Brar, H. S. Sandhu andS. S. Sandhu, Indian J. Chem., 18A (1979) 382.Google Scholar
  8. 8.
    A. S. Brar, H. S. Sandhu andS. S. Sandhu, Indian J. Chem., 19A (1980) 574.Google Scholar
  9. 9.
    A. S. Brar, H. S. Sandhu andS. S. Sandhu, Thermochimica Acta 41 (1980) 253.Google Scholar
  10. 10.
    J. G.Calvert and J. N.Pitts, Photochemistry, Academic Press 1967 p. 784.Google Scholar
  11. 11.
    J. F.Duncan and P. W. R.Wigley, J. Chem. Soc. 1120 (1966).Google Scholar
  12. 12.
    L. M. Epstein, J. Chem. Phys. 36 (1962) 2731.Google Scholar
  13. 13.
    E. Fluck, W. Kerler andW. Neuwirth, Chemie, 2 (1962) 277.Google Scholar
  14. 14.
    P. R.Brady, J. F.Duncan and K. K.Mok, Proc. R. Soc. London, 287 (1965).Google Scholar
  15. 15.
    J. Matas andT. Zemick, Phys. Letters, 19 (1965) 11.Google Scholar
  16. 16.
    A. N. Garg andP. S. Goel, J. Inorg. Nucl. Chem., 31 (1969) 697.Google Scholar
  17. 17.
    A. S. Brar, S. K. Date, H. S. Sandhu andS. S. Sandhu, Indian J. Chem., 19A (1980) 165.Google Scholar
  18. 18.
    J. C. Fanning andC. P. Monaghan, J. Phys. Chem., 82 (1978) 1045.Google Scholar
  19. 19.
    D. Raj andS. P. Puri, J. Chem. Phys., 50 (1969) 3185.Google Scholar
  20. 20.
    A. S. Brar andB. S. Randhawa, Radiochem. Radioanal. Letters 44 (1980) 377.Google Scholar
  21. 21.
    Y. Hazony, J. Chem. Phys., 45 (1966) 2664.Google Scholar
  22. 22.
    M. J. Rossiter, J. Phys. and Chem. Solids, 26 (1968) 775.Google Scholar
  23. 23.
    M. Eibschutz andU. Ganiel, Solid State Commun., 6 (1968) 271.Google Scholar
  24. 24.
    V. J. Bhide andS. Multani, Solid State Commun. 3 (1965) 271.Google Scholar
  25. 25.
    F. Voued, G. A. Swatzky andA. H. Morrish, Phys. Review, 167 (1968) 533.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1981

Authors and Affiliations

  • A. S. Brar
    • 1
  • H. Singh
    • 1
  • S. Brar
    • 1
  • B. S. Randhawa
    • 1
  1. 1.Chemistry DepartmentGuru Nanak Dev UniversityAmritsarIndia

Personalised recommendations