Degradation of an Acetylene Terminated Sulfone (ATS) resin

II. Under partially anaerobic conditions
  • W. T. K. Stevenson
  • I. J. Goldfarb
Article
  • 22 Downloads

Abstract

Using a custom built reactor, we modelled the decomposition of a high performance Acetylene Terminated Sulfone (ATS) resin, more precisely bis[4-(3-ethynyl phenoxy) phenyl] sulfone and its higher oligomers, under partially anaerobic conditions. The residue of thermal degradation was shown to possess a higher oxidative stability than early products of thermal degradation, which “scavanged” oxygen in the reactor to form secondary products such as carbon monoxide, carbon dioxide, and water: thus preventing direct oxidation of the resin. On removal of volatile products of thermal degradation, the carbonaceous char residue of thermal degradation is directly oxidized to carbon monoxide, carbon dioxide, and water.

Keywords

Phenyl Carbon Monoxide Oligomer Thermal Degradation Oxidative Stability 

Zusammenfassung

Unter Anwendung eines spezialangefertigten Reaktors modellierten wir die Zersetzung eines acetylenendständigen Sulfonhochleistungsharzes (ATS), genauer gesagt von bis[4-(3-ethinylphenoxy)phenyl]sulfon und seiner höheren Oligomere, unter partiellen anaeroben Bedingungen. Die im Endergebnis des thermischen Abbaues erhaltene Substanz verfügt über eine höhere oxidative Stabilität als die während des thermischen Abbaues vorher erhaltenen Produkte, die im Reaktor mit Sauerstoff sekundäre Produkte wie Kohlenmonoxid, Kohlendioxid und Wasser bilden; somit wird einer direkten Oxidation des Harzes vorgebeugt. Bei Entfernung der flüchtigen Produkte des thermischen Abbaues wird der kohlenstoffreiche Halbkoksrest des thermischen Abbaues direkt zu Kohlenmonoxid, Kohlendioxid und Wasser oxidiert.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. L. Koenig and C. M. Shields, J. Polym. Sci.: Polym. Phys. Ed., 23 (1985) 845.Google Scholar
  2. 2.
    J. J. Harrison and C. M. Selwitz, AFML-TR-79-4183.Google Scholar
  3. 3.
    W. T. K. Stevenson and I. J. Goldfarb, J. Thermal Anal., 36 (1990).Google Scholar
  4. 4.
    W. T. K. Stevenson, I. J. Goldfarb, and E. J. Soloski, Manuscript to be submitted to this Journal.Google Scholar
  5. 5.
    D. W. Breck, W. G. Eversol, R. M. Milton, T. B. Reed, and T. L. Thomas, J. Am. Chem. Soc., 78 (1956) 5963.Google Scholar
  6. 6.
    C. V. G. Nair and P. Vigendran, Vacuum, 27 (1) (1977) 549.Google Scholar
  7. 7.
    I. C. McNeill, Chapter 2 (p.43) in “Developments in Polymer Degradation — 1”, N. Grassie (Ed.), Applied Science Publishers, London, 1977.Google Scholar
  8. 8.
    Articles in Chemistry in Britain, March 1987: W.D. Woolley p. 215, P. J. Fardell and C. Lukas p. 221, P. J. Fardell, J. M. Murrell and M. G. Lunt p. 226, R. F. Simmons and E. Metcalfe p. 230, D. Price, A. R. Horrocks and M. Tunc p. 235.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1990

Authors and Affiliations

  • W. T. K. Stevenson
    • 1
  • I. J. Goldfarb
    • 1
  1. 1.AFWAL/MLBP Wright Patterson Air Force BaseDayton

Personalised recommendations