Abstract
The paper describes the synthesis of urethane methacrylate resins by reaction of tolylene diisocyanate (TDI), butanol-1 (B) and 2-hydroxyethylmethacrylate (HEMA) by a two step procedure. Characterisation was done using FT-IR, FT-NMR, Mass Spectroscopy. The effect of temperature on the UV-curing behaviour was investigated by differential photocalorimetry. An activation energy of 8.4 kJ/mole was found in the temperature range of 50–100°C. Free radical polymerisation in presence of benzoyl peroxide was also investigated. The polymers were stable upto 200°C in N2 atmosphere. A two step decomposition was observed in the temperature range of 200–500°C.
Zusammenfassung
Vorliegende Arbeit beschreibt die Synthese von Urethan-methacrylat-Harzen durch die Reaktion von Toluylendiisocyanat (TDI), Butanol-1 (B) und 2-Hydroxyethylmethacrylat (HEMA) in einem zweistufigen Herstellungsverfahren. Charakterisiert wurden die Produkte mittels FT-IR, FT-NMR und Massenspektroskopie. Anhand von Differentialfotokalorimetrie wurde der Einfluß der Temperatur auf das UV-Aushärtungsverhalten untersucht. Im Temperaturbereich 50–100°C wurde eine Aktivierungsenergie von 8.4 kJ/mol gefunden. Weiterhin wurde auch die Radikalkettenpolimerisation in Gegenwart von Benzoylperoxid untersucht. In Stickstoffatmosphäre sind die Polymere bis 200°C stabil. Im Temperaturbereich 200–500°C wurde eine zweistufige Zersetzung beobachtet.
Similar content being viewed by others
References
L. Kushner and R. S. Tu., Mod. Plast., 60 (1983) 87.
M. Koshiba, K. K. S. Hwang, S. K. Foley, D. J. Yarusso and S. L. Cooper, J. Mater. Sci., 17 (1982) 1447.
Shaow B. Lin, S. Y. Tsay, T. A. Speckhard, K. K. S. Hwang, J. J. Jezerc and S. L. Cooper, Chem. Eng. Comm., 30 (1984) 251.
C. Li, R. M. Nagarajan, C. C. Chiang and S. L. Cooper, Polym. Eng. & Sci., 26 (1986) 1442.
T. A. Speckhard, K. K. S. Hwang, S. B. Lin, S. Y. Tsay., M. Koshiba, Y. S. Ding and S. L. Cooper, J. Appl. Polym. Sci., 30 (1985) 647.
N. Levy and P. E. Massey, Polym. Eng. Sci., 21 (1981) 406.
R. G. Arnold, J. A. Nelson and J. J. Verbanc, Chem. Rev., 57 (1957) 47.
Author information
Authors and Affiliations
Additional information
The Instrument system of E. I. DuPont de Nemours & Co. is acknowledged for differential photocalorimeter studies.
Rights and permissions
About this article
Cite this article
Varma, J.K., Santhana Gopala Krishnan, P. & Choudhary, V. Synthesis and characterisation of urethane-methacrylates I. Journal of Thermal Analysis 36, 2611–2622 (1990). https://doi.org/10.1007/BF01913658
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01913658