Studies on crosslinking of EPDM-PE blends by thermoanalytical techniques

  • Achintya K. Sen
  • A. S. Bhattachcayya
  • P. P. De
  • Anil K. Bhowmick
Article

Abstract

The effect of blend ratio and peroxide concentration on crosslinking characteristics of EPDM-PE blends were studied by Differential Scanning Calorimetry, Brabender plasticorder and Rheometer. Crosslinking of EPDM-PE blends follows first order reaction kinetics. The curing exotherm increases but activation energy decreases with increase in EPDM content in the blends. The same however increases with the increase in concentration of DCP upto a certain level, while the activation energy is almost independent of peroxide concentration. The cure rate increases whereas optimum cure time and energy consumption for curing decrease with increase in the EPDM-PE ratio. A method for determination of crosslinking efficiency in the case of blend systems was developed from high temperature modulus to predict the properties and the curing behaviour of the blends.

Keywords

Activation Energy Differential Scan Calorimetry Calorimetry Reaction Kinetic Cure Time 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Zusammenfassung

Mittels DSC, Brabender Plasticorder und Rheometer wurde der Einfluß von Mischungsverhältnis und Peroxidkonzentration auf den Vernetzungsverlauf von EPDM-PE-Gemischen untersucht. Die Vernetzung von EPDM-PE-Gemischen verläuft nach einer Reaktion erster Ordnung. Je höher der Anteil von EPDM im Gemisch, um so exothermer ist die Vernetzung und um so kleiner ist die dazugehörige Aktivierungsenergie. Mit dem Anwachsen der DCP-Konzentration bis zu einem gewissen Niveau wächst der exotherme Charakter, während die Aktivierungsenergie fast unabhängig von der Peroxidkonzentration ist. Mit dem Anstieg des EPDM/PE-Verhältnisses wächst die vernetzungsgeschwindigkeit, während die optimale Vernetzungszeit und der Energieverbrauch für die Vernetzung sinken. Es wurde ein Verfahren zur Bestimmung der Vernetzungseffizienz bei Mischsystemen entwickelt, um Eigenschaften und Vernetzungsverhalten von Gemischen voraussagen zu können.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    T. R. Manley and M. M. Qayyum, Polymer, 12 (171) 176.Google Scholar
  2. 2.
    A. G. Anderpoulos and E. M. Kampouris, J. Appl. Polym. Sci., 31 (1986) 1061.Google Scholar
  3. 3.
    E. M. Kampouris and A. G. Anderpoulis, J. Appl. Polym. Sci., 34 (1987) 1209.Google Scholar
  4. 4.
    Y. A. Kao and P. J. Philips, Polymer, 27 (1986) 1669.Google Scholar
  5. 5.
    J. De Boer and A. J. Pennings, Polymer, 23 (1982) 1944.Google Scholar
  6. 6.
    Achintya K. Sen, B. Mukherjee, A. S. Bhattacharyya, L. K. Sanghi, P. P. De and Anil K. Bhowmick, communicated.Google Scholar
  7. 7.
    A. Y. Coran, in Anil K. Bhowick and H. L. Stephens (Eds.), Hand book of Elastomers — New Developments and Technology M. Dekker, 1988, Chap. 8.Google Scholar
  8. 8.
    A. Y. Coran, Rubber Chem. Technol, 61 91988) 281.Google Scholar
  9. 9.
    Achintya K. Sen, B. Mukherjee, A. S. Bhattacharyya, L. K. Sanghi, P. P. De and Anil K. Bhowmick, Thermochim. Acta, 157 (1090) 45.Google Scholar
  10. 10.
    D. W. Braizer and N. V. Schwartz, Thermochim. Acta, 39 (1980) 7.Google Scholar
  11. 11.
    A. Y. Coran and R. Patel, Rubber Chem. Technol, 53 (1980) 141.Google Scholar
  12. 12.
    A. Y Coran, B. Das and R. P. Patel, U. S. Patent 4, 130, 535, Dec. 19, 1978.Google Scholar
  13. 13.
    E. N. Kresge, in D. R. Paul and S. Newman (Eds.) Polymer blends, Vol. 2, Academic Press, N. Y. 1978, Chap. 20.Google Scholar
  14. 14.
    R. C. Keller, Rubber Chem. Technol., 61 (1988) 238.Google Scholar
  15. 15.
    L. D. Loan, Rubber Chem; Technol., 40 (1967) 149.Google Scholar
  16. 16.
    F. B. Baldwin and G. Verstrate, Rubber Chem., Technol., 45, (1972) 709.Google Scholar
  17. 17.
    V. Choudhury, H. S. Varma and I. K. Varma, J. Thermal Anal., 35 (1989) 257.Google Scholar
  18. 18.
    G. Widmann, J. Thermal Anal., 25 (1982) 45.Google Scholar
  19. 19.
    Brabender Instruction Manual No. 2762E, Sec. 2.5.Google Scholar
  20. 20.
    A. Posthuma De Boer and A. J. Pennings, J. Polym. Sci., Poly. Phys. Ed., 14 (1976) 187.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1991

Authors and Affiliations

  • Achintya K. Sen
    • 1
  • A. S. Bhattachcayya
    • 1
  • P. P. De
    • 2
  • Anil K. Bhowmick
    • 2
  1. 1.R & D Centre, Fort Gloster Industries Ltd (Cable Division)HowrahIndia
  2. 2.Rubber Technology CentreIndian Institute of TechnologyKharagpurIndia

Personalised recommendations