Specific heat of polytetrafluoroethylene and polychlorotrifluoroethylene within the temperature range 2.5–20 K

  • B. Terziiska
  • H. Madge
  • V. Lovtchinov
Article

Abstract

Low-temperature specific heat measurements on bulk technical polymer samples (polytetrafluoroethylene and polychlorotrifluoroethylene) were carried out between 2.5 and 20 K. In these experimental investigations a heat pulse method and an adiabatic vacuum calorimeter were used.

Keywords

Calorimeter Alla Polytetrafluoroethylene Polymer Sample Heat Pulse 

Résumé

On a effectué des mesures de chaleur spécifique à basse température, entre 2.5 et 20 K, sur des échantillons de polymères techniques en vrac (polytétrafluoroéthylène et polychlorotrifluoroé thylène), à l'aide d'une méthode par impulsions de chaleur et d'un calorimètre adiabatique sous vide.

Zusammenfassung

Messungen der spezifischen Wärme bei niedrigen Temperaturen wurden an technischen Polymerproben “alla rinfusa” (Polytetrafluoräthylen und Polychlortrifluoräthylen) zwischen 2.5 und 20 K durchgeführt. Bei diesen experimentellen Untersuchungen wurde eine Wärmepulsierungsmethode und ein adiabatisches Vakuumcalorimeter eingesetzt.

Резюме

Проведены низкотемп ературные измерения удельной теплоемкос ти технических полимерных образцов (политетрафторэтиле н и полихлортрифторэти лен) между 2.5 и 20 К. В проведенных исс ледованиях использо вали метод теплового импульса и адиабатический вакуумный калоримет р.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    R. E. Schramm, A. F. Clark andR. P. Reed, Monograph, 132, NBS, USA, 1973.Google Scholar
  2. 2.
    R. P. Reed, R. E. Schramm andA. F. Clark, Cryogenics, 13 (1973) 67.Google Scholar
  3. 3.
    W. Reese andJ. E. Tucker, J. Chem. Phys., 43 (1965) 105.Google Scholar
  4. 4.
    T. Scott andM. Giles, Phys. Rev. Lett., 29 (1972) 642.Google Scholar
  5. 5.
    Advances in Polymer Science, 7 (1970) 151.Google Scholar
  6. 6.
    W. J. Reese, Makromol. Sci. Chem., A3 (1969) 1257.Google Scholar
  7. 7.
    G. T. Furukawa, R. E. McCoskey andG. J. King, J. NBS, 49 (1952) 273.Google Scholar
  8. 8.
    R. J. Noer, C. W. Dempsey andJ. E. Gordon, Bull. Am. Phys. Soc., 4 (1959) 108.Google Scholar
  9. 9.
    W. Reese andJ. E. Tucker, J. Appl. Phys., 37 (1966) 3959.Google Scholar
  10. 10.
    A. D. Athougies, B. T. Peterson, G. L. Salinger andC. D. Swartz, Cryogenics, 12 (1972) 125.Google Scholar
  11. 11.
    I.I.Perepetchko, Properties of polymers at low temperatures, Moscow, Chemistry, 1977.Google Scholar
  12. 12.
    C. L. Choy, R. G. Hunt andG. L. Salinger, J. Chem. Phys., 52 (1970) 3629.Google Scholar
  13. 13.
    W. H. Stockmayer andC. E. Hecht, J. Chem. Phys., 21 (1953) 1954.Google Scholar
  14. 14.
    S. M. Genensky andG. F. Newell, J. Chem. Phys., 26 (1957) 486.Google Scholar
  15. 15.
    I. M. Lifshits, J. Experimental Theoret. Phys., 22 (1952) 475.Google Scholar
  16. 16.
    E. Leyarovski andB. Terziiska, Preprint 34, 1976, International Laboratory, Wroclaw, Poland.Google Scholar
  17. 17.
    B.Terziiska, Mechanical heat switch for low-temperature calorimeter, Author certificate 25729, 1974, Bulgaria.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1981

Authors and Affiliations

  • B. Terziiska
    • 1
  • H. Madge
    • 1
    • 2
  • V. Lovtchinov
    • 1
  1. 1.Institute of Solid-State PhysicsSofiaBulgaria
  2. 2.International Laboratory of High Magnetic Fields and Low TemperaturesWrocławPoland

Personalised recommendations