Difference method of evaluation of dynamic integral thermogravimetric curves in decomposition of polypropylene

  • J. Rychlý
  • L. Matisová-Rychlá
  • M. Vavreková
Article

Abstract

A new differential method of evaluating integral thermogravimetric records of the formation of volatile products during the degradation of polypropylene in air is presented. The method, applied to 0–100% conversion of the polymer to volatile products, may distinguish the initial presence of low molecular compounds in the polymer, as well as changes in the mechanism of degradation of the material.

Keywords

Polymer Physical Chemistry Inorganic Chemistry Polypropylene Difference Method 

Zusammenfassung

Es wird eine neue differentielle Methode zur Auswertung der die Bildung von flüchtigen Produkten während der Zersetzung von Polypropylen in Luft widerspiegelnden integralen thermogravimetrischen Kurven dargelegt. Mit der im Bereich 0–100% Konversion von Polymer zu flüchtigen Produkten anwendbaren Methode können sowohl die Anwesenheit niedermolekularer Verbindungen im Polymer als auch Veränderungen im Abbaumechanismus des Materials erkannt werden.

Резюме

Представлен новый ди фференциальный мето д вычисления интеграл ьных термогравиметр ических данных образования л етучих продуктов, образующи хся при распаде полипропилена в атмо сфере воздуха. Метод, использованный для о бласти 0–100%-ного превращения полимер а в летучие продукты, п озволяет различать начальное присутствие в полимере низкомолек улярных соединений, а также изменения в механизм е распада полимера.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    A. W. Coats andJ. P. Redfern, Nature, 201 (1964) 68.Google Scholar
  2. 2.
    H. H. Horowitz andG. Metzger, Anal. Chem., 35 (1963) 1464.CrossRefGoogle Scholar
  3. 3.
    C. D. Doyle, J. Appl. Pol. Sci., 5 (1961) 285.CrossRefGoogle Scholar
  4. 4.
    W. W. Wendlandt, Thermal Methods of Analysis, Sec. Edition, 19, Wiley Interscience Publication, New York, 1974, page 45.Google Scholar
  5. 5.
    J. H. Flynn andL. A. Wall, Journal of Research of NBS, Physics and Chemistry 70 (1966) 487.Google Scholar
  6. 6.
    J. Šesták, Thermochim. Acta, 7 (1973) 447.CrossRefGoogle Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1982

Authors and Affiliations

  • J. Rychlý
    • 1
  • L. Matisová-Rychlá
    • 1
  • M. Vavreková
    • 1
  1. 1.Polymer Institute of the Slovak Academy of SciencesBratislavaCzechoslovakia

Personalised recommendations