, Volume 33, Issue 4, pp 1171–1176 | Cite as

DSC investigation of high-strength and high-modulus polyethylene fibers

  • D. Zenke
  • R. Hirte
  • P. Weigel
Organic Chemistry, Polymers

Abstract

Fibers were produced from two commercial grade linear polyethylenes (PE) of different molecular weight by flow-induced crystallization. DSC measurements were carried out with an annealing and melting program lour melting peaks were found. The first peak, at the lowest temperature, can be identified with the melting of lamellar crystallized PE. Peak 2 corresponds to the melting of the main crystalline fraction of the fiber. and peaks 3 and 4 to the melting of constrained crystalline regions. The melting temperature depends on the molecular weight of the fiber material and on the drawing state.

Keywords

Polymer Molecular Weight Crystallization Polyethylene Melting Temperature 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Zusammenfassung

Durch strömungsinduzierte Kristallisation wurden Fasern aus zwei kommerziellen linearen Polyethylenen (PE) unterschiedlichen Molekulargewichts dargestellt. DSC-Messungen mit einem Temper- und Schmelzprogramm zeigten 4 Schmelzpeaks. Der erste — bei der niedrigsten Temperatur — entspricht dem Schmelzen von lamellar kristallisiertem PE. Peak 2 zeigt das Schmelzen des kristallinen Hauptanteils der Fasern, Peak 3 und 4 das Schmelzen der erzwungenen kristallinen Bereiche. Die Schmelztemperaturen hängen vom Molekulargewicht des Fasermaterials und seinem Verstreckungsgrad ab.

РЕжУМЕ

МЕтОДОМ кРИстАллИжА цИИ В стРУЕ пОлУЧЕНы ВОлОкНА Иж ДВУх пРОДА жНО ДОстУпНых сОРтОВ лИНЕИНОгО пОл ИЁтИлЕНА с РАжлИЧНыМ МОлЕкУльРНыМ ВЕсОМ. Д ск ИжМЕРЕНИь БылИ пРО ВЕДЕНы В пРОгРАММЕ ОтжИгА И п лАВлЕНИь. УстАНОВлЕН О ЧЕтыРЕ пИкА плАВлЕНИь. пЕРВы И пИк с НАИБОлЕЕ НИжкОИ тЕМпЕРАтУРОИ ИДЕНтИФИцИРОВАН кАк пИк плАВлЕНИь кРИстАллИ ЧЕскОгО пОлИЁтИлЕНА с лАМЕлльРНОИ стРУкт УРОИ. ВтОРОИ пИк сООтВ ЕтстВУЕт плАВлЕНИУ ОсНОВНОИ к РИстАллИЧЕскОИ ФРАкцИИ ВОлОкНА, А тРЕ тИИ И ЧЕтВЕРтыИ пИкИ - п лАВлЕНИУ кРИстАллИЧЕскИ НАпР ьжЕННых ОБлАстЕИ. тЕМпЕРАтУРы плАВлЕН Иь жАВИсьт От МОлЕкУл ьРНОгО ВЕсА пОлИЁтИлЕНОВОгО ВОл ОкНА И стЕпЕНИ ЕгО ВытьНУтОстИ.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    A. J. Pennings, J. Polym. Sci., Polym. Symp., 59 (1977) 55.Google Scholar
  2. 2.
    A. J. Pennings and J. Smook. J. Mat. Sci., 19 (1984) 3443.Google Scholar
  3. 3.
    A. Zwijnenburg, P. F. van Hütten, A. J. Pennings and H. D. Chanzy, Coll. et Polym. Sci., 256 (1978) 729.Google Scholar
  4. 4.
    J. Smook, I. C. Torfs, P. F. van Hutten and A. J. Pennings, Polym. Bull., 2 (1980) 293.Google Scholar
  5. 5.
    V. A. Marichin, L. P. Mjasnikova, D. Zenke, R. Hirte and P. Weigel, Polym. Bull., 12 (1984) 287.Google Scholar
  6. 6.
    T. Kunugi, I. Achi and M. Hashimoto, Kubunshi Ronbunshu, 38 (1981) 301.Google Scholar
  7. 7.
    A. J. Pennings and A. Zwijnenburg, J. Polym. Sci. Polym. Phys. Ed., 17 (1979) 1011.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1988

Authors and Affiliations

  • D. Zenke
    • 1
  • R. Hirte
    • 1
  • P. Weigel
    • 1
  1. 1.Institute of Polymer Chemistry “Erich Correns”TeltowG.D.R.

Personalised recommendations