Ni+Pd+Ga and Ni+Pd+in liquid alloys: Enthalpies of formation

Abstract

In order to fill the evident gap in the thermodynamic data of nickel-palladium-gallium and nickel-palladium-indium ternary alloys, the enthalpies of formation of these systems in the liquid state have been determined. This was achieved by means of a very high temperature calorimeter (T<1800 K), using the direct drop method, and based on analogous measurements of the respective binary alloys previously published. Complete automation of the calorimeter led to a good precision even at the highest temperatures. The enthalpies of formation of the ternary liquid alloys were measured between 1400 and 1600 K on the whole composition range. As in the limiting binary systems, enthalpies of formation are negative and non temperature dependent at any composition.

Zusammenfassung

Um die Lücke hinsichtlich thermodynamischer Daten von Nickel-Palladium-Gallium und Nickel-Palladium-Indium Legierungen zu füllen, wurden die Bildungsenthalpien dieser ternÄren Systeme im flüssigen Zustand bestimmt. Dies erfolgte mittels eines Kalorimeters für sehr hohe Temperaturen (T<1800 K), unter Verwendung der direkten Einwurfmethode auf der Basis früher veröffentlichter Messungen an den entsprechenden binÄren Systemen. Die Bildungsenthalpien der flüssigen ternÄren Legierungen wurden zwischen 1400 und 1600 K über den gesamten Zusammensetzungsbereich bestimmt. VollstÄndige Automation des Kalorimeters bewirkte hohe PrÄzision selbst bei den höchsten Temperaturen. Wie in den begrenzenden binÄren Systemen sind die Bildungsenthalpien negativ und bei allen Zusammensetzungen nicht temperaturabhÄngig.