Journal of thermal analysis

, Volume 8, Issue 3, pp 531–546 | Cite as

Solid state reactions between nickel(II) sulphide and oxides of manganese and iron

  • L. Gladman
  • F. G. Buttler
Article

Abstract

Thermogravimetry and differential thermal analysis have shown that, when nickel(II) sulphide and manganese or iron oxides are heated together, several reactions occur depending on the molar ratio of the reactants. Detailed examinations of these reactions have shown that there are a number of intermediate stages, including the formation of sulphates.

Keywords

Oxide Iron Polymer Sulfate Physical Chemistry 

Résumé

On montre par thermogravimétrie et analyse thermique différentielle que plusieurs réactions peuvent se produire suivant les rapports molaires des constituants lorsque l'on chauffe du sulfure de nickel(II) avec des oxydes de manganèse ou de fer. L'étude détaillée de ces réactions a mis en évidence un certain nombre d'étapes intermédiaires, avec formation de sulfates.

Zusammenfassung

Thermogravimetrie und Differentialthermoanalyse zeigen, daß bei gemeinsamer Erhitzen von Nickel(II)-Sulfid und Manganoder Eisenoxiden, in Abhängigkeit von dem Molarverhältnis der Reaktionspartner verschiedene Reaktionen stattfinden. Das eingehende Studium dieser Reaktionen zeigte das Auftreten einer Anzahl Zwischenstufen, darunter auch die Bildung von Sulfaten.

Резюме

С помощью термограви метрии и дифференциального т ермического анализа показано, что при совм естном нагревании су льфида никеля (II) с окислами ма гния или железа, протекает нес колько реакций в зави симости от молярного соотношен ия реагентов. Детальное исследова ние этих реакций пока зало, что имеется ряд промежут очных стадий, включая образование сульфатов.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    F. G.Buttler and A.Mitchell, PhD Thesis and unpublished work.Google Scholar
  2. 2.
    P. J. Galmés andC. Mataix, Afinidad, 27 (1950) 401.Google Scholar
  3. 3.
    E. Dönges, Z. Anorg. Chem., 253 (1947) 337.Google Scholar
  4. 4.
    A.Mitchell, PhD Thesis, (1969) 66.Google Scholar
  5. 5.
    Kun Li, R. R. Rothfus andA. H. Adey, Environ. Sci. Technol., 2 (1968) 619.Google Scholar
  6. 6.
    M. Atsukawa, Y. Nishimoto andK. Matsumoto, Tech. Rev. Mitsubishi Heavy Ind., 4 (1967), 33.Google Scholar
  7. 7.
    A.Mitchell, PhD Thesis, (1969) 14.Google Scholar
  8. 8.
    C.Malard, Bull. Soc. Chim. France, (1961) 2296.Google Scholar
  9. 9.
    R. Fruchart andA. Mitchell, Compt. Rend., 246 (1958) 1222.Google Scholar
  10. 10.
    T. V. Pantsulaya, Tr.Gruzinsk, Politekhn. Inst., 4 (1959) 59.Google Scholar
  11. 11.
    A.Mitchell, PhD Thesis, (1969) 42.Google Scholar
  12. 12.
    O.Kubaschewski, E. L.Evans and C. B.Alcock, Metallurgical Thermochemistry, 4th edition, Pergamon Press, 1967.Google Scholar
  13. 13.
    D. L. Hammick, J. Chem. Soc., 111 (1917) 379.Google Scholar
  14. 14.
    F. A.Cotton and G.Wilkinson, Advanced Inorganic Chemistry, 2nd edition, Interscience, 1966. p. 850.Google Scholar

Copyright information

© Wiley Heyden Ltd., Chichester and Akadémiai Kiadó, Budapest 1975

Authors and Affiliations

  • L. Gladman
    • 1
  • F. G. Buttler
    • 1
  1. 1.Department of ChemistryTeesside PolytechnicMiddlesbroughUK

Personalised recommendations