Journal of thermal analysis

, Volume 37, Issue 9, pp 2189–2203 | Cite as

Thermal properties of chalcogenide-halide glasses in the system: Ge-S-I

  • A. B. Seddon
  • M. A. Hemingway
Article

Abstract

Chaicogenide-halide glasses in the series [Ge0.3S0.7]100-xIx where 0≤x≤30 have been prepared and have potential applications as short length infrared optical fibres. Asx is increased the expansion coefficient increases, in addition the glass transformation temperature and onset temperature of mass loss both decrease as determined by differential scanning calorimetry and thermogravimetry, respectively. Melt viscosities in the range 107–1010.7 Pa s have been determined via penetration viscometry and isoviscous points are at lower temperatures asx increases. These results have been discussed in relation to known structural information and the fragility of the melts has been compared. Predicted fibre drawing temperatures tend to lie close to the onset of mass loss.

Keywords

Differential Scanning Calorimetry Mass Loss Calorimetry Thermogravimetry Optical Fibre 

Zusammenfassung

Es wurden Chalkogenid-Halogenid-GlÄser der Zusammensetzung [Ge0.3S0.7] 100-xIxmit 0≤x≤30 hergestellt. Sie besitzen potentielle Anwendungsmöglich-keiten als optische Fasern im kurzen IR-Bereich. Mit der Zunahme von x steigt auch der Ausdehnungskoeffizient. Wie durch DSC und TG ermittelt, nehmen jedoch dabei sowohl die Glasumwandlungstemperatur als auch die Anfangstemperatur des Massenverlustes ab. Die mittels Penetrationsviskosimetrie bestimmten ViskositÄten der Schmelze liegen im Bereich 107 bis 1010.7 und durch Ansteigen vonx werden isoviskose Punkte in Richtung niedrigerer Temperaturen verschoben. Die Ergebnisse wurden im Hinblick auf bekannte Informationen über die Struktur diskutiert und die Sprödigkeit der Schmelzen miteinander verglichen. Vorausgesagte Faserziehtemperaturen liegen nahe bei den Anfangstemperaturen für den Massenverlust.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. Savage, ‘Infrared optical materials and their anti-reflection coatings’, Adam Hilger Ltd., Bristol and Boston 1985.Google Scholar
  2. 2.
    T. Katsuyama and H. Matsumura, ‘Infrared optical fibres’, Adam Hilger, Bristol 1989.Google Scholar
  3. 3.
    S. Shibata, Y. Terunuma and T. Manabe, Mat. Res. Bull., 16 (1982) 703.CrossRefGoogle Scholar
  4. 4.
    P. W. Franceet al., ‘Flouride glass optical fibres’, Blackie, Glasgow 1990.Google Scholar
  5. 5.
    ‘Fluoride glasses’, Ed. A. E. Comyns, Critical Reports on Applied Chemistry, John Wiley & Sons, Chichester 1989,Vol.27.Google Scholar
  6. 6.
    H. Nasu and J. D. Mackenzie, Opt. Eng., 26 (1987) 102.Google Scholar
  7. 7.
    A. D. Pearson, Chapter 2 of ‘Modern aspects of the vitreous state 3’, Ed. J. D. Mackenzie, Butterworths, London 1964.Google Scholar
  8. 8.
    S. A. Dembrovskii, V. V. Kirilenko and Y. Buslaev, Neorg. Matter. Izv. Akad. Nauk USSR, 7 (1971) 328.Google Scholar
  9. 9.
    J. S. Sanghera, J. Heo and J. D. Mackenzie, J. Non-Cryst. Solids, 103 (1988) 155.CrossRefGoogle Scholar
  10. 10.
    B. Voigt and M. Wolf, J. Non-Cryst. Solids, 51 (1982) 317.CrossRefGoogle Scholar
  11. 11.
    Y. Kawamoto and S. Tsuchihashi, J. Amer. Ceram. Soc., 52 (1969) 626.Google Scholar
  12. 12.
    A. V. Cardoso and A. B. Seddon, ‘Penetration viscometry using a Thermal Mechanical analyser’, Glass Technology 32 (19911) 103.Google Scholar
  13. 13.
    Y. Kawamoto and S. Tsuchihashi, J. Amer. Ceram. Soc., 54 (1971) 131.Google Scholar
  14. 14.
    H. Vogel, Phys. Z., 22 (1921) 645.Google Scholar
  15. 15.
    G. S. Fulcher, J. Amer. Ceram. Soc., 6 (1925) 339.Google Scholar
  16. 16.
    S. W. Martin and C. A. Angell, J. Phys. Chem., 90 (1986) 6736.CrossRefGoogle Scholar
  17. 17.
    G. Lucovsky, J. P. de Neufville and F. L. Galeener, Phys. Rev. B, 9 (1974) 1591.CrossRefGoogle Scholar
  18. 18.
    G. Lucovsky, F. L. Galeener, R. C. Keezer, R. H. Geils and H. A. Six, Phys. Rev. B, 10 (1974) 5135.Google Scholar
  19. 19.
    R. Zallen, B. A. Weinstein and M. L. Slade, J. Phys., 42 (1981) 241.Google Scholar
  20. 20.
    Y. Kawamoto and C. Kawashima, Mat. Res. Bull., 17 (1982) 1511.CrossRefGoogle Scholar
  21. 21.
    J. Heo and J. D. Mackenzie, J. Non-Cryst. Solids, 113 (1989) 1.CrossRefGoogle Scholar
  22. 22.
    J. Heo and J. D. Mackenzie, J. Non-Cryst. Solids, 113 (1989) 246.CrossRefGoogle Scholar
  23. 23.
    C. A. Angell, J. Non-Cryst. Solids, 73 (1985) 1.CrossRefGoogle Scholar
  24. 24.
    W. C. Hasz, S. N. Crichton and C. T. Moynihan, Mat Sci Forum, 132–33 (1988) 589.Google Scholar
  25. 25.
    N. V. Sidgwick, ‘Chemical elements and their compounds’, Clarendon Press, Oxford 1950.Google Scholar

Copyright information

© Wiley Heyden Ltd, Chichester and Akadémiai Kiadó 1991

Authors and Affiliations

  • A. B. Seddon
    • 1
  • M. A. Hemingway
    • 1
  1. 1.School of MaterialsUniversity of SheffieldSheffieldUK

Personalised recommendations