Thermal conductivity of polytetrafluoroethylene and polytrifluorochloroethylene

  • Makoto Hattori
Originalarbeiten Polymere

Summary

Measurements of thermal conductivity were made on polytetrafluoroethylene and polytrifluorochloroethylene which were crystallized by various heat treatments. The variation of thermal conductivity with the degree of crystallinity can be explained qualitatively in terms of the difference of the mean free path. An approximate calculation of the mean free path for the amorphous polytrifluorochloroethylene was made. The calculation gives the value of the mean free path which is very close to the atomic distances in the polymer molecule.

Keywords

Thermal Conductivity Free Path Polytetrafluoroethylene High Polymer Crystalline Polymer 

Zusammenfassung

Die thermische Leitfähigkeit von Polytetrafluoräthylen und Polytrifluorchloräthylen wurde an Proben gemessen, die durch verschiedene Wärmebehandlungen kristallisiert wurden. Die Änderung der thermischen Leitfähigkeit mit dem Kristallisationsgrad kann qualitativ durch die Unterschiede der mittleren freien Weglänge erklärt werden. Eine abschätzende Berechnung der mittleren freien Weglänge des Polytrifluorchloräthylens wurde durchgeführt. Die berechneten Werte liegen nahe an den Atomabständen der Polymermoleküle.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1).
    Debye, P., Vorträge über die kinetische Theorie der Materie und der Elektrizität (Berlin 1914).Google Scholar
  2. 2).
    Peierls, R., Ann. Physik3, 1055 (1929).Google Scholar
  3. 3).
    Hattori, M., Bull. Univ. Osaka Pref. A9, 51 (1960).Google Scholar
  4. 4).
    Hattori, M., Chem. High Polymers (Kobunshi Kagaku), Japan17, 432 (1960).Google Scholar
  5. 5).
    Hattori, M., ibid.19, 32 (1962).Google Scholar
  6. 6).
    Hattori, M., ibid.19, 35 (1962).Google Scholar
  7. 7).
    Nishioka, A., J. Appl. Phys. (Oyo Butsuri), Japan25, 389 (1956).Google Scholar
  8. 8).
    Boyer, R. F., Changement de Phases (Paris 1952).Google Scholar
  9. 9).
    Sauer, J. A. andD. E. Kline, J. Polymer Sei.19, 207 (1955).Google Scholar
  10. 10).
    Furukawa, G. J., R. E. McCosky andG. J. King, J. Research Natl. Bur. Standards49, 273 (1952).Google Scholar
  11. 11).
    Bunn, C. W. andE. R. Howells, Nature174, 549 (1954).CrossRefGoogle Scholar
  12. 12).
    Eucken, A., Ann. Physik34, 185 (1911).Google Scholar
  13. 13).
    Kittel, C., Phys. Rev.75, 972 (1949).CrossRefGoogle Scholar
  14. 14).
    Altenburg, K., Z. Physik. Chem.202, 14 (1953).Google Scholar
  15. 15).
    Hoffman, J. D., J. Amer. Chem. Soc.74, 1696 (1952).CrossRefGoogle Scholar

Copyright information

© Dr. Dietrich Steinkopff Verlag 1962

Authors and Affiliations

  • Makoto Hattori
    • 1
  1. 1.Department of Applied Chemistry, College of EngineeringUniversity of Osaka PrefecturePrefelcture Sakai-shiJapan

Personalised recommendations