Studies in condensed metaphosphates

Part III. Sodium metaphosphate and its derivatives with copper, lead and zinc
  • R. C. Mehrotra
  • V. S. Gupta
Originalarbeiten Polymere

Synopsis

Derivatives with the general formula
$$(Na_x M_{1 - x/2} PO_3 )_n ,$$
wherex is 2/3, 1/2; and 1/3 and M is Ca, Ba, Zn, Cu or Pb, have been synthesised. The extent of reaction has been studied thermogravimetrically. The number average\((\bar M_n )\) and viscosity average\((\bar M_w )\) molecular weights of these compounds have been determined. The specific conductance has been plotted against equivalent concentration, which shows a slight bend at lower concentration. Equivalent conductivity against square root of equivalent concentration\(\sqrt c \) curves show a sharp rise at lower dilution. This is explained due to the association of counter-ions with poly-anions because of high charge density around the latter. The plots of A vs\(\sqrt c \) can be reduced to linear ones on a log-log scale.

Keywords

Talc Metaphosphate Potassium Chloride Solution NaZn Electrometric Titration 

Zusammenfassung

Verbindungen mit der allgemeinen Formel
$$(Na_x M_{1 - x/2} PO_3 )_n ,$$
, wobei x 2/3,1/2 und 1/3 ist, und M Ca, Ba, Zn, Cu oder Pb, wurden synthetisiert. Das Ausmaß der Reaktion wurde thermogravimetrisch untersucht. Das Zahlenmittel\((\bar M_n )\) und das Viskositätsmittel\(\bar M_w \) (Gewichtsmittel) der Molekulargewichte dieser Verbindungen wurden ebenfalls bestimmt. Die spezifischen Leitfähigkeiten zeigen, aufgetragen gegen die Äquivalentkonzentration, ein leichtes Abbiegen bei geringen Konzentrationen. Die Äquivalentleitfähigkeit, gegen die Quadratwurzel der Äquivalentkonzentration aufgetragen, zeigt bei Verdünnung einen scharfen Anstieg. Man kann dies als Folge einer Assoziation der Gegenionen mit den Polyanionen erklären, als Folge der hohen Ladungsdichte um letztere. Die Auftragungen A gegen\(\sqrt c \) lassen sich in der log-log-Skala auf lineare Beziehungen reduzieren.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1).
    Mehrotra, R. C. andV. S. Gupta, J. Polymer. Sci.54, 613 (1961).CrossRefGoogle Scholar
  2. 2).
    Mehrotra, R. C. andV. S. Gupta, ibid.55, 81 (1961).CrossRefGoogle Scholar
  3. 3).
    Van Wazer, J. R. andC. F. Callis, Chem. Revs.58, 1011 (1958).CrossRefGoogle Scholar
  4. 4).
    Morey, G. W., J. Amer. Chem. Sec.74, 5783 (1952).CrossRefGoogle Scholar
  5. 5).
    Ohashi, S. andJ. R. Van Wazer, J. Amer. Chem. Soc.81, 830 (1959).CrossRefGoogle Scholar
  6. 6).
    Wall, F. T. andR. H. Dormeus, J. Amer. Chem. Soc.76, 868 (1954).CrossRefGoogle Scholar
  7. 7).
    Tammann, G., J. pract. Chem. (2),45, 417 (1892).Google Scholar
  8. 8).
    Van Wazer, J. R., C. F. Callis andP. G. Arvan, Chem. Revs.54, 777 (1954).CrossRefGoogle Scholar
  9. 9).
    Strauss, U. P., E. H. Smith andP. L. Winemann, J. Amer. Chem. Soc.75, 3935 (1953).CrossRefGoogle Scholar
  10. 10).
    Strauss, U. P. andT. L. Tritler, ibid.77, 1473 (1955).CrossRefGoogle Scholar
  11. 11).
    Chatterjee, A. C. andH. N. Bhargava, J. Polymer Sci.35, 236 (1959).Google Scholar
  12. 12).
    Samuelson, O., Svensk. Kem. Tid.56, 343 (1944).Google Scholar
  13. 13).
    Gustavson, K. H. andA. Larsson, Acta. Chem. Scand.5, 1221 (1951).CrossRefGoogle Scholar
  14. 14).
    Van Wazer, J. R., J. Amer. Chem. Soc.72, 647 (1950).CrossRefGoogle Scholar
  15. 15).
    Bawn, C. E. H., The Chemistry of High Polymers, p. 35 (New York 1948).Google Scholar
  16. 16).
    Billmeyer, Fred. W. Jr., Text Book of Polymer Chemistry, p. 117, 132 (New York 1957).Google Scholar
  17. 17).
    Chatterjee, A. C. andH. N. Bhargava, Kolloid-Z.170, 116–123 (1960).CrossRefGoogle Scholar
  18. 18).
    Davies, C. W. andC. B. Monk, J. Chem. Soc.1949, 413.Google Scholar
  19. 19).
    Monk, C. B., ibid,1949, 423, 427.Google Scholar
  20. 20).
    Kern, W., Z. Phys. Chem. A.181, 249 (1938).Google Scholar
  21. 21).
    McFarlane, R. jr. andR. M. Fuoss, J. Polymer Sci.23, 603 (1957).Google Scholar
  22. 22).
    Basu, S. andP. C. Das Gupta, J. Colloid Sci.7, 53 (1952).CrossRefGoogle Scholar
  23. 23).
    Fuoss, R. M., Disc. Faraday Soc.11, 125 (1951).CrossRefGoogle Scholar
  24. 24).
    Fitzgerald, E. B. andR. M. Fuoss, J. Polymer Sci.14, 329 (1954).CrossRefGoogle Scholar

Copyright information

© Dr. Dietrich Steinkopff Verlag 1962

Authors and Affiliations

  • R. C. Mehrotra
    • 1
  • V. S. Gupta
    • 1
  1. 1.Chemical LaboratoriesUniversity of GorakhpurGorakhpur, U. P.India

Personalised recommendations