Dislocations in Fe-3·2% Si alloy single crystals deformed by bending are studied in this paper. The specimens were cut parallel to the slip plane into platelets, polished, and studied in places at various distances from the neutral plane with an electron microscope. A large number of jogs of various sizes was found on screw dislocations. Many loops are formed by the motion of dislocations with jogs and by the stopping of moving dislocations by obstacles. Some of them grow as a result of stress. The activity of sources on large jogs is stopped at an early stage by a cross slip. The formation and growth of loops increases the dislocation density and causes the growth of slip bands.
Abstract
В работе исследуются дислокации в монокристаллах Fe-3,2% Si, деформируемых на изгиб Образцы вырезались параллельно плоскости скольжения в форме пластинок, полировались и просматривались под электронным микроскопом в местах, расположенных на различных расстояниях от нейтральной плоскости. На винтовых дислокациях было обнаружено большое количество порогов различной величины. Благодаря движению дислокаций по порогам и захвату движущихся дислокаций на дефектах, образуется большое количество петель. Некоторые из них растут под влиянием напряжения. Образование дислокаций на больших порогах остановлено в начальной стадии поперечным скольжением. Возникновение и рост петель увеличивает плотность дислокаций и обусловливает рост зон скольжения.
Similar content being viewed by others
References
Šesták B., Kroupa F., Libovický S.: Czech. J. Phys.B12 (1962), 369.
A brief reference to this paper is made in the general report by Keh A. S., Weissmann S.: Deformation Substructure in Body Centered Cubic Metals, Conference on the Impact of Transmission Electron Microscopy on Theories of the Strength of Crystals, University of California, July 1961.
Libovický S.: Čs. čas. fys.A 11 (1961), 493 (in Czech).
Šesták B.: Hutnické listy14 (1959), 223 (in Czech).
Šesták B., Libovický S.: Czech. J. Phys.B 11 (1961), 444.
Šesták B., Libovický S.: Czech. J. Phys.B 12 (1962), 131.
Amelinckx S., Dekeyser W.: J. Appl. Phys.29 (1958), 1000.
Johnston W. G., Gillman J. J.: J. Appl. Phys.31 (1960), 632.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Gemperle, A., Rozsíval, M. & Šesták, B. Electron microscope study of dislocations in slip bands of bent Fe-3·2% Si alloy single crystals. Czech J Phys 12, 555–560 (1962). https://doi.org/10.1007/BF01689438
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01689438