The lattice spacings of equilibrium solid solutions of silver in aluminium

Abstract

This paper describes the measured dependence of the lattice spacings of equilibrium Al-Ag solid solutions on temperature and composition. The form of the lattice spacing composition curve is found to differ considerably from that for the supersaturated Al-Ag solid solutions. The differences between the spacings of equilibrium and quenched Al-Ag solid solutions plotted against the electron concentration yield a curve similar to that constructed from the analogous measurements on Al-Zn given by Ellwood. The differences can be attributed to the influence of changes accompanying the increased solute clustering introduced by quenching the solid solutions into the supersaturated state.

Abstract

Эта работа описывает измерение зависимос ти постоянных решетки р авновесных твердых растворов Al-Ag от темпер атуры и состава. Было о бнаружено, что форма зависимост и постоянной решетки о т состава у равновесн ых твердых растворов Al-Ag отличаетс я от формы той же зависимости у п ересыщенных твердых растворов. Разность постоянных решетки равновесных и закале нных твердых раствор ов Al-Ag, представленная как ф ункция электронной концентрации (т. е. числ а валентных электрон ов, приходящихся на один атом в твердом растворе), имеет анало гичную форму как у сис темы Al-Zn, для которой эта зависимо сть была построена по изм ерениям, проведенным Эллвудом. Возникшие разницы в п остоянных решетки у равновесны х и пересыщенных твер дых растворов можно объя снить влиянием изменений, обусловле нных повышенным обра зованием групп атомов легирую щего элемента при закалке твердого раствора до пересыще нного состояния.