Wärme - und Stoffübertragung

, Volume 14, Issue 3, pp 211–215 | Cite as

Influence of surface treatments on the total normal emittance of AISI316 stainless steel

  • C. Isetti
  • E. Nannei
Article

Abstract

Total normal emittance measurements have been performed on AISI 316 L samples in temperature range 400–1050 K. Two sets of mirror finished samples, with the same average roughness, have been obtained by means of polishing wheels and metallographical procedure and then etched with different acid mixtures.

Emittance tests were carried out on all samples oxidized at 1050 K for a period of 3 and 14 hours.

Experimental results show a remarkable influence of surface finishing on the total normal emittance of oxidized samples. The influence of surface finishing becomes negligible when an electropolishing process is made after etching.

Keywords

Stainless Steel Apply Physic Finished Sample Surface Treatment Acid Mixture 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Einfluß der Oberflächenbehandlung auf den normalen Gesamtemissionsgrad von rostfreiem Stahl AISI 316

Zusammenfassung

Der normale Gesamtemissionsgrad an Proben von AISI 316 L wurde für Temperaturen von 400 bis 1060 K gemessen. Zwei Sätze von spiegelblanken Proben mit gleicher Rauhigkeit wurden mit Hilfe von Polierscheiben oder durch eine metallographische Prozedur vorbehandelt und dann mit verschiedenen Säuremischungen geätzt. An allen oxidierten Proben wurde der Emissionsgrad bei 1050 K über 3 und 14 Stunden gemessen. Die Versuche zeigen einen starken Einfluß der Oberflächenbehandlung auf den Emissionsgrad der oxidierten Proben, der jedoch zu vernachlässigen war, wenn die Proben nach dem Ätzen elektropoliert wurden.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Bennet, H.E.: Influence of surface roughness, surface damage, and oxide films on emittance. NASA SP-55 (1964) 145–151Google Scholar
  2. 2.
    Wong, H.Y.; Aggarwal, S.R.: Total hemispher- ical emittance of stainless steel AISI 321. Iron Steel Inst. (1971) 635–637Google Scholar
  3. 3.
    Isetti, C.; Nannei, E.; Pisoni, C: Oxidation and roughness effects on the total normal emittance of stainless steel. High Temp. -High Pressures 11 (1979) 393–397Google Scholar
  4. 4.
    Krinninger, H.: Messung des Emissionsvermögens austenitischer Stähle für den Schnellen Natriumgekühlten Brutreaktor. Wärme- und Stoffübertrag. 3 (1970) 139–145Google Scholar
  5. 5.
    Brannon, Jr. R.R.; Goldstein, R.J.: Emittance of oxide layers on a metal substrate. J. Heat Transf. (1970) 257–263Google Scholar
  6. 6.
    Donovan, T.M.; Ashley, E.J.; Bennet, H.E.: Effect of surface damage on the reflectance of germanium in the 2650–10000 OHA region. J. Opt. Soc. Am. 53 (1963) 1403–1409Google Scholar
  7. 7.
    Zanzucchi, P.J.; Duffy, M.T.: Surface damage and the optical reflectance of single-crystal silicon. Appl. Opt. 17 (1978) 3477–3481Google Scholar
  8. 8.
    Ruffino, G.; Pisoni, C.: An apparatus for emissivity measurements. High Temp. High Pressures 8 (1976) 419–424Google Scholar
  9. 9.
    Alfano, G.: Apparent thermal emittance of cylindrical enclosures with and without diaphragms. Int. J. Heat Mass Transf. 15 (1972) 2671–2674Google Scholar
  10. 10.
    Samuels, L.E.: Modern ideal on the mechanical polishing of metals. Res. Appl. Ind. 13 (1960) 344–349Google Scholar

Copyright information

© Springer-Verlag 1980

Authors and Affiliations

  • C. Isetti
    • 1
  • E. Nannei
    • 1
  1. 1.Istituto di Fisica Tecnica e Impianti TermotecniciGenovaItaly

Personalised recommendations