Abstract
In 1966 when studying the recrystallization of austenite after high speed hot forming, PluhaŘ and Zuna observed a phenomenon which consisted in the nucleation and new grain growth right in the recrystallized matrix, following a pronounced grain coarsening. The phenomenon was called the second recrystallization. On the basis of the present-day knowledge the second recrystallization can be considered as a specific case of metadynamic or static recrystallization. Its characteristic feature — grain coarsening before refining — offers an analogy with the recrystallization after small deformations.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
PluhaŘ J., Zuna P.:in Martensitic Transformation. čSVTS, Ostrava, 1966.
PluhaŘ J., Zuna P.: JISI207 (1969) 58.
PluhaŘ J., Zuna P., Orlová, A.: Rev. Met. Mem. Sci.66 (1969) 207.
Zuna P., PluhaŘ J., Janovec J., Orlová A.: Kovové Mater.12 (1974) 47.
Zuna P., PluhaŘ J.: Kovové Mater.14 (1976) 199.
Kheifets R. G., Marek I. M., Senina T. V.: Izv. VUZ Chernaya Metallurgia8 (1977) 115.
Kheifets R. G., Rezchik N. V., Marek I. M., Senina T. V.: Metallovedenie i termicheskaya obrabotka metallov (1982) 37.
Hensger K. E., Klimanek P., Martin U.: Czech. J. Phys. B35 (1985) 1633.
Petkovic R. A., Luton M. J., Jonas J. J.: Acta Metall.27 (1979) 1633.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zuna, P., PluhaŘ, J. & Macek, K. Recrystallization of selected metals and alloys with fcc lattice after high speed hot forming. Czech J Phys 38, 388–391 (1988). https://doi.org/10.1007/BF01605410
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01605410