Abstract
Transmission electron microscopy (TEM), quantitative texture analysis by means of neutron diffraction (QTA) and X-ray diffraction profile analysis (XDPA) were used to study the microstructure changes occurring in high-speed hot rolling (\(\dot \varphi \)≦1500 s−1;T=1073 K) of high-alloy stainless steel X8CrTi17 (ferrite) and X8CrNiTi18.10 (austenite). The investigations indicate that at higher deformation rates recrystallization due to adiabatic overheating becomes an important process of microstructure formation.
Similar content being viewed by others
References
Schubert A.: Thesis. Academy of Mining, Freiberg (GDR), 1985.
Hensel A., Oehlstöter G., Lietzmann K.: Neue Hütte27 (1984) 37.
Hensel A., Spittel Th.: Kraft- und Arbeitsbedarf bildsamer Formgebungsverfahren. Leipzig, 1978.
Barthel M., Klimanek P., Stoyan D.: Czech. J. Phys. B35 (1985) 265.
Hanisch K.-H., Klimanek P., Stoyan D.: Cryst. Res. & Technol.20 (1985) 921.
Schubert A., Hensger K.-E., Klimanek P., Matthies S., Mücklich A.:in Proc. 7th ICOTOM. Noorwijkerhout (Netherlands), 1984, p. 133.
Schubert A., Klimanek P., Hensger K.-E.: Textures and Microstructures, in press.
Kleinstück K., Tobisch J., Betzl M., Mücklich A., Schläfer D., Schläfer U.: Krist. & Tech.11 (1976) 409.
Barthel M., Klimanek P., Hensger K.-E.: Czech. J. Phys. B38 (1988) 377.
Kato K., Saito Y., Sakai T.: Trans. ISIJ24 (1984) 1050.
Sakai T., Saito Y., Kato K.: Trans ISIJ27 (1987) 520.
Gorelik S. S.: Recrystallization in Metals and Alloys. MIR Publ., Moscow, 1981.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Klimanek, P., Hensger, K.E., Schubert, A. et al. Microstructure changes in high-speed hot rolling of steel rods. Czech J Phys 38, 373–376 (1988). https://doi.org/10.1007/BF01605406
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01605406