Abstract
Transient creep of pure and commercial aluminium was studied under a constant stress of 18·6 MPa at different temperatures ranging from 613 to 698 K. The anomalous values of transient creep parametersβ, n ranging from 0·003–0·055 (±0·001) and 0·5–1·0 (±0·05) respectively, which were found in this temperature rangs, might bs ascribed to the superplastic behaviour of pure and commercial aluminium. The activation energy of transient creep for pure Al was found to be about (2·4 +0·07) × 10−22) kJ/atom. characterizing a dislocation glide-cross slipping mechanism.
Similar content being viewed by others
References
Friede1 J.: Dislocations, Pergamon Press Ltd., London, 1964, p. 304, 317.
Waytt O. H.: Proc. Phys. Soc.B 66 (1953) 459.
Gilman J. J.: J. Appl. Phys.36 (1965) 3195.
Ahlquist C. N., Nix W. D.: Acta Metall.19 (1971) 373.
Mott N. F.: Phil. Mag.44 (1953) 742.
Barrett C. N., Nix W. D.: Acta Metell.13 (1965) 1247.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Nagy, M.R., El-Salam, F.A., Habib, N.D. et al. Anomalous behaviour of transient creep in commercially pure aluminium. Czech J Phys 31, 937–940 (1981). https://doi.org/10.1007/BF01603791
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01603791