The effect of age hardening on the critical resolved shear stress (CRSS) of Cu-0-9 at.% Ti single crystals was measured at 77 K. The scatter of the CRSS values is due to the different Ti concentration in individual samples. The procedure is given to correct this scatter based on the assumption of diffusion controlled new phase formation.
Similar content being viewed by others
References
Chellman D. J., Ardell A. J., Proc. ICSMA 4, Nancy (France) 1976, 219.
Ardell A. J., Chellman D. J., Munjal V., Proc. ICSMA4, Nancy (France) 1976, 209.
Munjal V., Ardell A. J., Acta Met.24 (1976), 827.
Amin K. E., Gerold V., Kralik G., J. Mater. Sci.10 (1975), 1519.
Ham F. S., J. Phys. Chem. Solids6 (1958), 335.
Iijima Y., Hoshino K., Hirano K., Met. Trans.8A (1977), 997.
Cornie J. A., Datta A., Soffa W. A., Met. Trans.4 (1973), 731.
Labusch R., phys. stat. sol.41 (1970), 659.
Laughlin D. E., Cahn J. W., Acta Met.23 (1975), 329.
Pešička J., Czech. J. Phys.28B (1978), 410.
Kamenská A., Diploma Thesis MFF UK, Prague 1977.
Author information
Authors and Affiliations
Additional information
It is the authors' pleasure to thank Dr. M.Saxlová, who kindly helped them with many stimulative comments during the preparation of the present paper.
Rights and permissions
About this article
Cite this article
Kratochvíl, P., Pešička, J. The evaluation of age hardening in copper crystals with not identical concentration of titanium. Czech J Phys 29, 584–588 (1979). https://doi.org/10.1007/BF01600180
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01600180