Local order of icosahedral quasicrystals studied by Mössbauer spectroscopy

Abstract

Thermodynamically stable Al-Cu-Fe and Fe-doped ferromagnetic Al-Cu-Ge-Mn icosahedral quasicrystals are studied by⁵⁷Fe transmission Mössbauer spectroscopy and X-ray diffraction experiments. Al₆₅Cu₂₀Fe₁₅ quasicrystalline alloy was subjected to a mechanical grinding (MG) for up to 800 hours in a ball mill. Presence of the amorphous phase which co-exists with the quasicrystalline one is revealed in the early stage of MG. Mössbauer measurements were performed on icosahedral Al₄₀Cu_10−x Ge₂₅Mn₂₅Fe _x quasicrystal (xε〈0.1; 3〉) in a temperature range from 10 K to 548 K. It was found that a magnetic transition occurs at about 30 K which is far belowT _c reported in the literature. It is concluded that AlGeMn ferromagnet which is present in the samples does not affect the magnetic transition observed and the transition is an intrinsic property of the Al-Cu-Ge-Mn host alloy.