Abstract
The hardening effect of Li+, Na+, K+ and Rb+ impurities in polycrystalline AgCl was investigated. With increasing concentration of the impurities the flow stress increases and the plasticity decreases. By doping with a few ppm of Rb+ AgCl becomes very brittle. Comparing the results with the statistical theory of solid solution hardening, deviations were found.
Similar content being viewed by others
References
Luhman W. J., Gorum A. E., Acta Met.7 (1959), 685.
Kabler M. N., Miller M. G., Slifkin L. M., J. Appl. Phys.34 (1963), 1953.
Fleischer R. L., Acta Met.9 (1961), 996.
Labusch R., phys. stat. sol.41 (1970), 659.
Dean J. A., Lange's Handbook of Chemistry, New York 1974.
Mason W. P., Physical acoustics III. Part B, New York 1965.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Vávra, F., Burian, P. Influence of monovalent cationic impurities on plasticity of AgCl. Czech J Phys 27, 1385–1388 (1977). https://doi.org/10.1007/BF01588768
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01588768